The paper describes the growth of a germanium (Ge) film on a thin relaxed Ge-rich SiGe buffer.The thin Ge-rich SiGe buffer layer was achieved through a combination of ultrahigh vacuum chemical vapor deposition (UHVCVD) SiGe epitaxial growth and SiGe oxidation. A lower Ge content strained SiGe layer was first grown on the Si (001) substrate and then the Ge mole fraction was increased by oxidation. After removal of the surface oxide, a higher Ge content SiGe layer was grown and oxidized again. The Ge mole fraction was increased to 0.8 in the 50 nm thick SiGe layer. Finally a 150 nm thick pure Ge film was grown on the SiGe buffer layer using the UHVCVD system. This technique produces a much thinner buffer than the conventional compositionally graded relaxed SiGe method with the same order of magnitude threading dislocation density.