The moving boundary non-equilibrium segregation during recrystallization and the influence of pre-deformation in Fe-30%Ni Alloy at1000℃ was investigated by the
Employing Simulated Annealing Algorithm (SAA) and many measured data, a calculation model of work roll wear was built in the 2 800 mm 4-high mill of Wuhan Iron