【摘 要】
:
以魔芋葡甘聚糖和羧甲基纤维素钠为主要原料,添加丙三醇为增塑剂,乳酸为改性剂,结合微波处理工艺,采用流延成型的方法制备出魔芋葡甘聚糖/羧甲基纤维素钠共混膜。通过FT-IR、
论文部分内容阅读
以魔芋葡甘聚糖和羧甲基纤维素钠为主要原料,添加丙三醇为增塑剂,乳酸为改性剂,结合微波处理工艺,采用流延成型的方法制备出魔芋葡甘聚糖/羧甲基纤维素钠共混膜。通过FT-IR、X-射线衍射对共混膜进行性能表征,同时测定了共混膜的吸水率、力学性能和降解率。结果表明:膜有较好的降解性能和细胞相容性,作为一种潜在的术后防粘连材料将具有良好的应用前景。
Konjac glucomannan and sodium carboxymethyl cellulose as the main raw material, add glycerol as plasticizer, lactic acid as modifier, combined with microwave treatment process, the use of casting method to prepare konjac glucomannan / Sodium carboxymethyl cellulose blend film. The blends were characterized by FT-IR and X-ray diffraction. The water absorption, mechanical properties and degradation rate of the blends were measured. The results showed that: the membrane has good degradation performance and cell compatibility, as a potential postoperative anti-adhesion material will have a good prospect.
其他文献
以苦基氯为初始原料,经过叠氮化,脱氮环化合成4,6-二硝基苯并氧化呋咱.4,6-二硝基苯并氧化呋咱与无机钠盐反应合成其钠盐.通过红外图谱、1 H-NMR、13C-NMR、元素分析、有机质
通过开环聚合、酯化反应等方法制备聚乙二醇-聚己内酯(PEG-b-hPCL)线性-超支化嵌段共聚物,利用核磁(1 H-NMR)、凝胶渗透色谱(GPC)等表征。DSC结果表明超支化PCL的熔程较长;测
通过紫外光谱考察了造纸黑液中碱木质素在离子液体氯化1-丁基-3-甲基咪唑([BMIm]C1)作用时在水中的平衡溶解度及其对碱木质素的助溶作用.实验结果表明,水中碱木质素的平衡溶
写作是小学语文教学的重要部分,然而,在实际教学中,写作是很多语文老师教学的一个“短板”,同时也是很多学生的弱项.常言道:“读书破万卷,下笔如有神”,很多语文老师意识到可
以聚乙二醇1540为模板剂,Al(NO3)3为铝源,(NH3)2CO3为沉淀剂,Ca(NO3)2和Mg(NO3)2分别作为改性剂,采用沉淀法一步合成钙镁改性的有序介孔氧化铝(OMA-Ca、OMA-Mg)。通过XRD、TE
通过种子乳液聚合的方法合成了不同玻璃化转变温度(Tg)聚合物乳液,然后将不同T_g的乳液按照不同比例进行混拼,得到不同理论T_g值的共混乳液。对共混乳液的Tg、断裂伸长率、拉
研究了用改性梧桐落叶作生物吸附剂去除地下水中的氟离子,考察了溶液pH、氟离子初始质量浓度、反应时间对氟离子去除率的影响,并采用Box-Behnken响应面法对吸附条件进行优化
初中阶段的学生,身处由小学基础向高中拔高的过渡时期,这段时期正是他们思维方式从具体向抽象转变的重要阶段。因此,懵懂的他们对外界的一切事物都有着好奇心,有着强烈的求知
采用纺粘法成功制备了夜光非织造布,分析比较了含相同比例发光材料的夜光机织布与夜光非织造布的性能差异.通过分析得出结论:与夜光机织布相比,夜光纺粘非织造布的纤维表面颗
采用500nm和20nm的SiO2粒子,通过表面改性使其分别具有氨基和环氧基,利用氨基和环氧基的反应使500nm和20nm的SiO2粒子形成复合粒子,制备了具有微纳米双尺寸粗糙度的超疏水表