用电子束蒸发NiO粉末的方法在ITO导电玻璃上制备电变色氧化镍薄膜,并将薄膜置于200-500℃的空气环境中进行1h热处理.用XRD分析了薄膜的结构,电化学方法测试了薄膜的电致变色性能,发现热处理对薄膜微观结构的影响较小,而对薄膜的致色效率及致色与消色态的透射率动态变化范
The method of electron beam evaporation NiO powder prepared on ITO conductive glass electrochromic nickel oxide film, and the film placed in an air environment at 200-500 ℃ for 1h heat treatment. The structure of the film was analyzed by XRD. The electrochromic properties of the film were tested by electrochemical method. The results showed that the effect of heat treatment on the microstructure of the film was small, but the change of the color rendering efficiency and the transmittance of the color-forming and the color- Fan