【摘 要】
:
采用一步合成法在Al-MIL-53骨架中引入功能化基团—NH2、—Cl、—NO_2和—OH,研究了各基团对AlMIL-53上CO_2吸附性能的影响。结果表明:引入上述4种基团明显增强了Al-MIL-53骨
【机 构】
:
上海电力学院数理学院,华东师范大学化学与分子工程学院,
论文部分内容阅读
采用一步合成法在Al-MIL-53骨架中引入功能化基团—NH2、—Cl、—NO_2和—OH,研究了各基团对AlMIL-53上CO_2吸附性能的影响。结果表明:引入上述4种基团明显增强了Al-MIL-53骨架和CO_2分子间的相互作用强度。除—OH外,3种基团的存在提高了材料的CO_2吸附容量。—OH功能化Al-MIL-53的低CO_2吸附容量可能是由于—OH的引入造成孔堵塞所致。
The functional groups -NH2, -Cl, -NO_2 and -OH were introduced into the framework of Al-MIL-53 by one-step synthesis method to study the influence of each group on the adsorption properties of CO 2 on AlMIL-53. The results showed that the introduction of the above four groups significantly enhanced the intensity of the interaction between the Al-MIL-53 framework and CO 2 molecules. In addition to -OH, the presence of three kinds of groups increased the CO 2 adsorption capacity of the material. The low CO 2 adsorption capacity of -OH functionalized Al-MIL-53 may be due to plugging of the pores due to the introduction of -OH.
其他文献
以花生壳为碳源,氯化锌为活化剂制备了花生壳基活性炭材料。采用扫描电子显微镜(SEM)、比表面积及孔径分析仪和电化学工作站分别对材料的结构和电化学性能进行了测试。结果表
以硅酸盐玻璃为基底,酸性SiO2溶胶、碱性SiO2溶胶和3种不同酸碱比例的SiO2溶胶混合液为浸渍拉膜液,通过提拉镀膜工艺,再经十六烷基三甲氧基硅烷(HDTMS)修饰制备了疏水涂层.研
为了提高硅酸盐基陶瓷涂层对金属基体的腐蚀防护性能,在304不锈钢表面制备了4种不同Al含量的硅酸盐基陶瓷涂层(简记为S1-S4).运用扫描电子显微镜对涂层在3.5% NaCl溶液中浸泡
以尿素和硝酸锌作为反应物,采用均匀沉淀法制备ZnO的前驱物,300℃焙烧制备ZnO颗粒,再将其分散在氧化石墨烯(GO)中制备ZnO/GO复合物,考察复合物在可见光下降解亚甲基蓝的光催
学习科学文化知识重要的是培养学生学习的兴趣. 俗话说"兴趣是最好的老师冶,如果一个学生对所学知识感兴趣,就会化被动学习为主动学习,以学习知识为乐,进而在快乐中主动学习
为了提高废橡胶粉改性沥青的各个性能,首先采用不同目数废胶粉组合改性沥青,研究复合目数对改性沥青的影响;其次,添加助剂改善沥青与废橡胶粉的相容性,提高储存稳定性,通过正
选择耐水性优异的双酚A型二酐与双酚A型二胺作为反应的单体,通过二步聚合得到分子量较高的端酸酐聚酰亚胺,利用酸酐活性,接枝上酰基己内酰胺活性基团,得到PI改性尼龙树脂.黏
通过采用3因素3水平的正交试验方法分别考察水灰比(W/C=0.3、0.32、0.35)、碳纳米管(CNT)掺量(wCNT=0.1%、0.2%、0.3%)、KH550掺量(wKH55=0.1%、0.3%、0.5%)对硅烷防水剂改性
目的探讨神经内镜下经鼻蝶入路切除垂体瘤的手术技巧及优缺点分析.方法回顾性分析沈阳市第一人民医院神经外科2007~2013年收治的39例垂体瘤患者的临床资料,均采用神经内镜下
常用聚氨酯泡沫材料一般通过添加含卤素的阻燃剂提高其阻燃性,该种类型的泡沫材料氧指数不高,燃烧时会产生有毒浓烟.利用异氰酸酯的三聚反应,并合成了两种芳烃聚醚,将耐温性