A new type of cement was prepared with ground limestone powder,blastfurnace slag,steel slag and gypsum without calcination.The fraction of ground limestone powder in the cement was as high as 40 wt%-60 wt%without Portland clinker.All of its physical prope
【机 构】
：
Key Laboratory of Silicate Materials Science and Engineering Ministry of Education,Wuhan University
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
A new type of cement was prepared with ground limestone powder,blastfurnace slag,steel slag and gypsum without calcination.The fraction of ground limestone powder in the cement was as high as 40 wt%-60 wt%without Portland clinker.All of its physical properties can meet the requirements of masonry cement standards.The impact of limestone content on physical properties of the cement and determined its impact on law was investigated.The steel slag can excit the aquation activity of this cement effectively,and the influence of its quantity on the strength of the materials was studied,which shows that the optimum quantity of mixing is 10%.By way of changing the different content of the lime stone by quartzy sample,the law of the compression strength and the PH value was determined,confirming that the lime stone can promote the early aquation of the slag and improve the early strength.The main hydration product of this cement is calcium aluminate hydrate, ettringite and calcium silicate hydrate,as indicated by XRD and SEM analysis.
其他文献
The normal asphalt index test,DSR test,FTIR and the GPC distribution analysis of molecular weight on the extraction and recovery of asphalt of the gussasphalt,SMA extraction and recovery of asphalt and the rotary-thin-film-oven-aged asphalt above 240℃were
50CrVA cold-rolled spring steel strip was used to fabricate the diaphragm of the automotive horn.The material parameters which were taken into account in the design of the dia-phragm involve elongation,elastic limit,Young\'s modulus,yield strength and t
Particle reinforced Sn-Zn based composite solders were obtained by adding Cu powders to Sn-9Zn melts. The microstructure analysis reveals that in situ Cu_5Zn_8 particles are formed and distributed uniformly in the composite solders. The strength and plast
Red mud was activated to be a mineral admixture for Portland cement by means of heating at different elevated temperatures from 400 ℃ to 700 ℃. Results show that heating was ef-fective, among which thermal activation of red mud at 600 ℃ was most effective
Astabilizedsoilstructureformation model wasintroduced. In ordertoformcompact stabilized soil structure, cementitious hydrates were needed to wrap and bind the soil aggregates.Meanwhile, expansible hydrates were needed to squeeze and fill the pores, especi
Hardened cement paste was subjected to the flexural loading and wet-dry cycles in sea water.The degradation of microstructures was obtained using scanning electron microscope(SEM),and the energy dispersive spectrum(EDS)analysis was carried to analyze the