The prism specimens of corroded concrete were subjected to uniaxial compressive load to develop the stress-strain model. Compared to the un-corroded concrete, the mechanical prop- erties of corroded concrete, such as peak strength, Young’s modulus, and residual deformation, et al are degraded. The concrete, which were subjected to the aggressive media in the environment, were resulted in randomly distributed pre-loading flaws and defects. The propagation of these corrosion flaws during the procedure of loading was the main reason of degradation of corroded concrete properties. By the application of the statistic theory of continuum damage, the compressive stress-strain curve of corroded concrete was simulated. The initial damage factor was introduced to represent the corrosive effects of different media. The present damage constitutive model agreed well with the test results.
Compared to the un-corroded concrete, the mechanical prop- erties of corroded concrete, such as peak strength, Young’s modulus, and residual deformation, et The concrete, which were subjected to the aggressive media in the environment, were resulted in randomly distributed pre-loading flaws and defects. The propagation of these corrosion flaws during the procedure of loading the the main reason of degradation of corroded concrete By the application of the statistic theory of continuum damage, the compressive stress-strain curve of corroded concrete was simulated. The initial damage factor was introduced to represent the corrosive effects of different media. The present damage constitutive model agreed well with the test results.