The oxidation behaviors of Ni-16Cr-xAl(x=4.5%, 9.0%, mass fraction) superalloy foams in air at 1 000 °C were investigated. The effects of Al content on the resistance to high temperature oxidation were examined. The oxidation mechanisms of the foams