【摘 要】
：
Alumina sols with a mlar ratio of 1: 50 between aluminum sec- butoxide ( ASB ) and H2 O werefabricated by adding various amounts of nitric acid.The particle sha
【机 构】
：
Key Laboratory of Silicate Materials Science and Engineering
【基金项目】
：
Foundation for University Key Teacher of the Ministry of Education;教育部重点研究项目
论文部分内容阅读
Alumina sols with a mlar ratio of 1: 50 between aluminum sec- butoxide ( ASB ) and H2 O werefabricated by adding various amounts of nitric acid.The particle shape, zeta potential, polydispersity and effective particle size of alumina sol were examined by a TEM, a zeta PALS granularity analyzer and a zetaPALS zeta potential analyzer, respectively.By analyzing the change of zeta potential and double- layer thickness with nitric acid concentration, the potential energy curves of colloidal particles were mapped on the basis of DLVO theory, and the effects of nitric acid concentration on the stability of alumina sols were intensively studied.The results show that for the alumina sols with a mol ratio of 1: 50 between ASB and H2 O, the total interaction energy of the colloidal particle is at a maximum when the nitric acid concentration is 0.22 mol/ L.Therefore, the stability of the colloid reaches optimum at the nitric acid concentration of 0.22 mol/L.
其他文献
A stochastic model for simulating the microstructure formation of Mg alloy AZ91 during solidification was developed based on the finite element method(FEM) for
The assessment for bearing capacity of corroded RC members is one of the main component of durability study on RC structure. But few researches had been develop
La doped nanocrystalline TiO2 photocatalyst was developed by sol-gel method. The prepared La-TiO2 photocatalysts with anatase phases were characterized by X-ray
Computational studies of a class of potentially stable high-spin biradicals that two-atom-three-electron spin centers SC units connected by heterocycles FC and
The compressive experiments of two kinds of ceramic foams were completed. The results show that the behavior of ceramic foams made by organic filling method is
In order to improve the prediction capability of spring-back in aluminum sheet metal forming, the influence of the plastic deformation on elastic modulus is con
The ceramic coating formed on AZ91 magnesium alloy by micro-arc oxidation (MAO) was characterized. The results show that the ceramic coating(3.4-23 μm in thick
By electrical resistance tomography (ERT) the cross sectional profiles of gas hold-up in a φ56mm bubble colunmn are obtained with four designs of gas sparger.
Fouling-resistant ceramic-supported polymer composite membranes were developed for removal of oil-in-water (O/W) microemulsions. The composite membranes were fe
Free radical co-polymerization was employed to synthesize co-poly carboxylate (PC) superplasticizers with different amount of carboxyl and methyl polyethylene g