5. Effect of Filler Composition on the Brazing of Alumina to Copper Using Ultrasonic Wave

Effect of Filler Composition on the Brazing of Alumina to Copper Using Ultrasonic Wave

来源 :材料科学技术：英文版 | 被引量 : 0次 | 上传用户：cclone

【摘 要】

：

An ultrasonic wave was applied during brazing of alumina to Cu. First alumina was metallized by applying ultrasonicwave in braze bath. Then the metallized alumi

【作 者】

：

Khalid M. HAFEZ Masaaki NAKA 

【机 构】

：

Joining&,WeldingResearchInstitute

【出 处】

：

材料科学技术：英文版

【发表日期】

：

2003年z1期

【关键词】

：

Alumina Copper ULTRASONIC waves Fracture stress Microstructure BRAZING 

下载到本地 , 更方便阅读

下载此文 赞助VIP

声明 : 本文档内容版权归属内容提供方 , 如果您对本文有版权争议 , 可与客服联系进行内容授权或下架

论文部分内容阅读

An ultrasonic wave was applied during brazing of alumina to Cu. First alumina was metallized by applying ultrasonicwave in braze bath. Then the metallized alumina was brazed with Cu using the same filler alloy. The filler used wereZn-Al alloys and Zn-Sn A

其他文献

新闻侵权与新闻舆论监督“优先保护”原则

期刊

新闻侵权新闻舆论监督"优先保护"原则舆论监督权诽谤法美国

Formation of Ultrafine Metal Particles and Metal Oxide Precursor on Anodized Al by Electrolysis

镍被交流电解免职在在磷酸阳极化生产的艾尔的多孔的氧化物电影的毛孔扔。极其细小的条形的 Ni 粒子在毛孔被形成。同时， Ni 氧化物先锋的一部电影在多孔的氧化物电影的表面上

期刊

Indole and Its Derivatives as Corrosion Inhibitors for C-Steel during Pickling

在 10% 盐酸答案的 C 钢的三种类型的腐蚀在缺席和禁止者的存在被调查了，吲哚(A) ，吲哚乙酸(B) ，吲哚奶油的酸(C) ，和 3 乙酰吲哚(D) ，由在不同温度的重量损失大小(30 ～ 7 0 ℃) 。

期刊

Indirect Measurement of Material Thermal and Mechanical Properties during Welding

By means of a newly developed non-contact detecting method, electronic speckle pattern interferometry (ESPI), a method of determining material property data dur

期刊

MATERIALpropertiesWELDINGDISPLACEMENTfieldNUMERICALsimulationESPI

Effect of Respective Additions of Ga, Zr and Combined Additions of Co, Ga, Zr on Magnetic Properties

期刊

Preparation and Microstructure of a Si-Mo Fused Slurry Coating on Carbon/Carbon Composites for Oxida

A coating of composition Si-40Mo (wt pct) was prepared by fused slurry coating method on the two-dimensional carbon/carbon (2D-C/C) composite to improve oxidati

期刊

Electron Beam Irradiation-induced Diffusion of Oxygen in the Al Particle Encapsulated by A1203 Shell

Transportation of oxygen from AI203 shell to the encapsulated AI core under the electron beam irradiation was achieved by field emission gun transmission electr

期刊

电子束三氧化二铝放射反应铝粒子

Formation and Oxidation Resistance of Silicide Coatings for Mo and Mo-Based Alloys

The forming process of silicide coatings on pure Mo and Mo-base alloys, obtained by the gasphase deposition method, has been studied by examining the microstruc

期刊

钼合金氧化阻抗硅化物沉积作用

Amorphous Alloy Forming in the Fe-Hf Films by IBAD Technique

Amorphization in the Fe/Hf multilayered films was achieved by Ar+ ion beam assisted deposition (IBAD) technique. The Ar+ ion energy used was from 4 to 12 keV. S

期刊

Forming Mechanism of Gaseous Defect in Ti-48A1-2Cr-2Nb Exhaust Valves Formed with Permanent Mold Cen

A method combining theoretical analysis with experiment is adopted and the flowing process of Ti-48AI-2Cr-2Nb alloy melt poured in a permanent mould during the

期刊