【摘 要】
:
Homogeneous HA coating materials were prepared on porous titanium by the low-temperature combustion synthesis. It was found that the mechanical properties of th
【机 构】
:
School of Materials Science and Engineering,Northwest Institute for Nonferrous Metal Research
论文部分内容阅读
Homogeneous HA coating materials were prepared on porous titanium by the low-temperature combustion synthesis. It was found that the mechanical properties of the specimen depend on the coating process and the heat treatment, and the bending strength would be reduced during the coating process but could be improved by heat treatment. The effects of the temperature during heat-treatment on the phase composition and microstructure of the as-prepared coating, and the bending strength of the specimen were investigated by XRD and SEM.The experimental results show that in the coating process, slight oxidation of the substrate may give rise to a drop in bending strength; however, it could be increased by the reaction of HA and TiO2, and the sintering of the coating during heat treatment. The HA particles in the coating, with very fine sized particles, were pretty active and would decompose at 800 ℃ .
其他文献
Magnetite was modified by reaction with alkaline solution containing Co2+ and Fe2+ to obtain a cobalt ferrite layer on the surface of particles.The influences o
Evolution of microstructures of alloy MlNi3.75 Co0.75 Mn0.3Al0.2 (Ml-La-rich mischmetal) during the electrochemical hydriding-dehydriding process was studied by
Measurements of wave heights with image sequences from a Charged Coupled Device(CCD) camera were made. Sinusoidal, as well as unidirectional and directional, wa
As one of promising clean coal technologies used to reduce pollutant emission and CO2 discharge, cogasification has been extensively investigated. In this paper
For increased and various communication requirements of modem applications on embedded systems, general purpose protocol stacks and protocol models are not effi
The high-temperature oxidation-resistant MoSi2 coating on the Nb substrate was prepared by slurry firing.The structure,compositions and phase distribution of th
The bubble deformation processes were reported when gas was injected into polymer melt flow field in another paper, the experiments showed that the deformation
Secret sharing and digital signature is an important research area in information security and has wide applications in such fields as safeguarding and legal us
The residual stresses on the surface of the differently ground and polished silicon nitride ceramics were measured using X-ray diffraction and identified by SEM
The main cause to the deactivation of ZSM-5 catalyst, used for oxidation of benzene to phenol (BTOP)by nitrous oxide, is that the carbon deposition on the catal