【摘 要】
:
Owing to the inhomogeneous state resulting from the doping of a small number of Eu ions into La4/3Sr5/3Mn2O7, from the resulting single crystal (La0.8Eu0.2)4/3S
【机 构】
:
Department of Physics, Baotou Normal University, Baotou 014030, China“,”State Key Laboratory of Magn
论文部分内容阅读
Owing to the inhomogeneous state resulting from the doping of a small number of Eu ions into La4/3Sr5/3Mn2O7, from the resulting single crystal (La0.8Eu0.2)4/3Sr5/3Mn2O7 we have observed the magnetization jump, the resistivity jump, as well as the relaxation phenomena. For (La0.8Eu0.2)4/3Sr5/3Mn2O7, it has a very delicate ground state due to the interplays among spin, charge, orbital, lattice degrees of freedom. Consequently, the magnetization state is sensitive to temperature, magnetic field, as well as time. Meanwhile, the evolution of the magnetization with time shows a spontaneous jump when both the temperature and the magnetic field are constant. Similar step-like behaviours are also observed in resistivity. All these results suggest that Eu doping can greatly modulate the physical properties of La4/3Sr5/3Mn2O7 and cause such interesting behaviours.
其他文献
Two-dimensional (2D) closed-cavity single quantum well (SQW) and multiple quantum well (MQW) structures are proposed based on the traditional 2D open-cavity SQW
本试验以“山农0431×鲁麦21”为父母本形成的重组自交系群体的177个系为材料,利用已有的图谱进行苗期耐盐相关性状的性状的QTL分析。主要结果如下:
设置三个处理,每个处
Based on the second-order moments,this paper derives an analytical expression of the M2 factor of four-petal Gaussian beam.The results show that the M2 factor i
This paper studies the light scattering and adsorption of nanocrystalline TiO2 porous films used in dye-sensitized solar cells composed of anatase and/or rutile
An efficient two-step quantum key distribution (QKD) protocol with orthogonal product states in the n( )n(n ≥ 3) Hilbert space is presented. In this protocol,
This paper examines the quantization of mesoscopic circuit including Josephson junctions.Following Feynman’s assumption,via the Hamilton dynamic approach and b
Zn0.75Co0.25O films are fabricated via reactive electron beam evaporation.The influence of growth temperature on the microstructural,optical and magnetic proper