对 DIAMOND324- H药芯焊丝+ SSD Ⅱ焊剂(相当于 Lincoln224)进行了堆焊工艺试验研究。在化学分析、金相分析、硬度试验、焊后热处理工艺研究的基础上,成功地完成了大型卷板机夹送辊的生产制造,并取得了良好的效果,为新型堆焊材料的进一步推广应用奠定了基础。
The DIAMOND324-H flux cored wire + SSD Ⅱ flux (equivalent to Lincoln224) was studied by the welding process. Based on the research of chemical analysis, metallographic analysis, hardness test and post-weld heat treatment, the successful manufacture of pinch rolls for large-scale coiling machine has been achieved and good results have been achieved. The new surfacing material is further popularized Application laid the foundation.