Experiment on seamless tubes of aluminum alloy A6063 with initial thickness deviation of 0-20% was conducted through a free hydraulic bulging with tube ends fre
【机 构】
：
School of Mechanical Engineering,School of Mechatronic Engineering
论文部分内容阅读
Experiment on seamless tubes of aluminum alloy A6063 with initial thickness deviation of 0-20% was conducted through a free hydraulic bulging with tube ends free. The influence of initial thickness deviation on the cross-section profile, thickness distribution, maximum internal pressure and maximum radial expansion was investigated. FEM simulation was also performed in order to examine and help explaining the experimental results. The results indicate that the internal pressure and maximum internal pressure appear to be little influenced by the initial thickness deviation, and that the cross-section profile of the bulged tube changes diversely and can not be a perfect circle. The results also suggest that the increase in initial thickness deviation may lead to a remarkable decrease in maximum radial expansion, and a rapid increase in thickness deviation and the center eccentricity of the inner and outer profiles.
其他文献
Free radical co-polymerization was employed to synthesize co-poly carboxylate (PC) superplasticizers with different amount of carboxyl and methyl polyethylene g
Alumina sols with a mlar ratio of 1: 50 between aluminum sec- butoxide ( ASB ) and H2 O werefabricated by adding various amounts of nitric acid.The particle sha
A laboratory study was undertaken to investigate drying shrinkage and cracking sensitivity subjected to restrained shrinkage of mortar containing fly ash (FA),
The coating of ZnS∶Mn by Sb-doped SnO2 using an co-precipitation process was reported. ZnS∶Mn phosphor particles were prepared by solid reaction with ZnS and
Although H.264 video coding standard provides several error resilience tools, the damage caused by error propagation may still be tremendous. This work is aimed
TiB2P/Al composite was successfully fabricated by squeeze casting technology. Its mechanical and tribological properties were evaluated. The elimination of Ti-A
The single-crystalline nickel nanorods with narrow size distribution and better magnetic properties were synthesized by thermal decomposition of nickel hydroxid
A new anodizing process,which does not contain chromate but can improve the corrosion resistance of magnesium alloys significantly,was developed using a microar
The effect of cobalt on chemical segregation and solution process in three nickel base single crystal superalloys was investigated. Three alloys containing the
The microstructure and superconducting properties of Bi-2223 superconductor fabricated in high magnetic fields were investigated. The results shows that the Bi-