The magnesium-lithium (Mg-Li) alloy exhibits two phase structures between 5.7wt% and 10.3wt% Li contents, consisting of the a (hcp) Mg-rich and the β (bee) Li-
【机 构】
：
School of Materials and Metallurgy
论文部分内容阅读
The magnesium-lithium (Mg-Li) alloy exhibits two phase structures between 5.7wt% and 10.3wt% Li contents, consisting of the a (hcp) Mg-rich and the β (bee) Li-rich phases, at room temperature. In the experiment, Mg-5Li-2Zn, Mg-9Li-2Zn,Mg-16Li-2Zn, Mg-22Li-2Zn, Mg-5Li-2Zn-2Ca, Mg-9Li-2Zn-2Ca, Mg-16Li-2Zn-2Ca, and Mg-22Li-2Zn-2Ca (wt%) were melted.During the melting process, the flux, which was composed of lithium chloride (LiCI) and lithium fluoride (LiF) in the proportion of 3:1 (mass ratio) and argon gas were used to protect the alloys from oxidation. The mierostructure, mechanical properties, and cold-rolling workability of the wrought alloys were studied. The crystal grain of the alloys (adding Ga) is fine. The hardness of the studied alloys decreases with an increase in element Li. The density of the studied alloys is in the range of 1.187 to 1.617 g/cm3 The reduction of the Mg-16Li-2Zn and Mg-22Li-2Zn alloys can exceed 85% at room temperature. The Mg-9Li-2Zn-2Ca alloy was heat treated at 300℃ for 8, 12, 16, and 24 h, respectively. The optimum heat treatment of the Mg-9Li-2Zn-2Ca alloy is 300~Cx12h by metallographic observation and by studying the mechanical properties of the alloys.
其他文献
A modified solid-state route was attempted to prepare Y0.95 Eu0.05PO4 PDP phosphor,involving milling a powdered mixture of YCl3,EuCl3,and (NH4)2HPO4 and calcini
Polyaniline(PAn) doped with multiple sulfonic acid system of dodecylbenzenesulfonic acid(DBSA) and sulfosalicylic acid(SSA) was synthesized by emulsion polymeri
The silicon assistant method to increase the reaction yield of carbothermal reduction of silica at a lower temperature is reported. The effect of silicon on the
The variations of intrinsic coercivity and remanence of sintered Nd-Fe-B magnets with ultra-high intrinsic coercivity were investigated.The results showed that
The effects of various factors on the flow speed of interdendritic melt were analyzed in detail in the process of continuous casting slabs. When the solid-liqui
The space time spreading,superimposed training sequences,and space-time coding are used to present a multiple input and multiple output(MIMO)systems model,and a
To improve the durability as well as to reduce the cost of anodes, the IrO2+MnO2 composite coating anodes for NaC10 production were prepared by thermal decompos
Al-20Sn-1 Cu powders were prepared by gas atomization in an argon atmosphere with atomizing pressures of 1.1 and 1.6 MPa.The characteristics of the powders are
At present,all hydrogen storage alloys are poisoned by hydrogen mixed with CO,CO2,etc,which decreases the hydrogen storage property sharply.Zr-Co based hydrogen
It is well known that the periodic performance of spread spectrum sequence heavily affects the correlative and secure characteristics of communication systems.T