Perovskite [(Ba0.6Sr0.4)TiO3]-[2SiO2-B2O3]-[K2O]-La2O3 glass was prepared by conventional melt quench method. The differential thermal analysis (DTA) was performed on glass sample in the temperature range from 100℃ to 1000℃ by different heating rate to st