In order to precisely control the final temperature of molten steel in RH (Ruhrstahl Heraeus)-TOP blowing refining, the final temperature prediction models of molten steel in RH-TOP blowing refining process for Interstitial Free (IF) steel production were established under the condition of oxygen blowing and non-oxygen blowing respectively. The results show that the beginning molten steel temperature of refining and the amount of added scrap were influential factors, the baking temperature in vacuum chamber was a factor that had small influence. When the model was operated, the hitting probability was above 95% (under the condition of both oxygen blowing and non-oxygen blowing) of prediction deviation of ±10 ℃. The accuracy is analyzed.
In order to precisely control the final temperature of molten steel in RH (Ruhrstahl Heraeus) -TOP blowing refining, the final temperature prediction models of molten steel in RH-TOP blowing refining process for Interstitial Free (IF) steel production were established under the condition of oxygen blowing and non-oxygen blowing respectively. The results show that the beginning molten steel temperature of refining and the amount of added scrap were intial factors, the baking temperature in vacuum chamber was a factor that had small influence. , the hitting probability was above 95% (under the condition of both oxygen blowing and non-oxygen blowing) of prediction deviation of ± 10 ° C. The accuracy is analyzed.