研究制备了具有高阻尼性能的受阻酚AO-80/丁腈橡胶复合材料样品,采用动态粘弹性测试得到了损耗因子tan δ与温度T的关系曲线。分析表明,随着受阻酚含量的增加,tan δ峰的位置向高温方向移动,tan δ峰的峰值也逐渐提高;利用pvT高压膨胀计对样品进行了测试,采用Tait方程研究了其压力-体积-温度(pvT)性能,对此计算出Tait方程中的相应参数。结果表明,由Tait方程计算所得的pvT理论关系与定性实验结果一致,具有较好的规律性,即对AO-80/丁腈橡胶复合体系b1值随AO-80量的增加而逐渐降低,“,”AO-80/Nitrile rubber composites were prepared and characterized. According to DMTA experiments, the peak of tan δ moved towards higher temperature and the peak height of tan δ was also enhanced while the quantity of AO-80 increased. The pvT data was obtai