对比研究了纳米TiO_2和钠基蒙脱石(MMT)对不饱和聚酯树脂(UPR)包覆层凝胶时间、固化时间、固化放热峰、黏度的影响。结果表明,在相同温度下,纳米复合体系的凝胶时间、固化时
论文部分内容阅读
对比研究了纳米TiO_2和钠基蒙脱石(MMT)对不饱和聚酯树脂(UPR)包覆层凝胶时间、固化时间、固化放热峰、黏度的影响。结果表明,在相同温度下,纳米复合体系的凝胶时间、固化时间和固化放热峰都低于空白UPR体系;复合体系的黏度随着纳米填料含量的增加而增大,添加纳米TiO_2的复合体系黏度要低于添加MMT的复合体系黏度。
The effects of nano-TiO 2 and sodium montmorillonite (MMT) on the gel time, curing time, curing exothermic peak and viscosity of unsaturated polyester resin (UPR) coating were studied. The results showed that the gelation time, curing time and curing exothermic peak of nanocomposite were lower than that of blank UPR at the same temperature. The viscosity of nanocomposite increased with the content of nanofiller increasing. The nanocomposite The viscosity of the system is lower than the viscosity of the composite system added MMT.
其他文献
大学文化是高校核心竞争力的重要组成部分,高校存在重物质建设轻精神建设,在适应大学生思想特点及网络媒体时代方面存在一定困难.天津外国语大学通过多途径进行大学文化建设
应用静电纺丝技术和热处理方法制备了疏水性聚乙烯醇/硅钨酸(PVA/SiW_(12)),随后利用光还原反应使银纳米粒子(AgNPs)沉积在PVA/SiW_(12)纤维上的三元复合纳米材料上。采用XPS
以纳米氧化锌(ZnO)为载体,采用稀土离子掺杂的方法制备了Ce/ZnO纳米复合抗菌剂。通过TEM、XRD等技术对样品进行表征,结果表明:制备的Ce/ZnO复合粉体是一种纳米复合抗菌剂,粒
采用射频磁控溅射法在Si(111)衬底上制备多组分掺杂ZnO薄膜,研究了衬底温度和氧分压对Bi、Cr、Sb、Mn和Co掺杂ZnO薄膜的晶体结构、表面形貌及电学性能的影响。结果表明:随着
以聚偏氟乙烯(PVDF)/N,N二甲基乙酰胺(DMAc)/正辛醇/水为制膜体系,采用粗糙基底辅助相转化法制备PVDF疏水性多孔膜。考察了水蒸汽诱导时间对膜结构、表面浸润性和透过性能的
新时期高校党建工作要树立品牌,以品牌活动吸引人,以鲜明主题教育人,以特色制度凝聚人,充分发挥高校党组织战斗堡垒和党员先锋模范带头作用.凯里学院积极探索党建工作新模式,
药物缓控释体系的研究在材料化学与生物医药领域备受关注。凝胶体系由于其良好的结构可控性、生物相容性和环境响应性等特点,使其成为一类重要的药物缓控释载体。刺激响应性
采用原位聚合的方法制备了聚噻吩插层钽钛酸钾导电聚合物纳米复合材料,通过X射线衍射(XRD)、红外光谱(IR)、热重分析(TG)和电化学等手段对复合材料进行了研究.研究结果表明:
大学是向国家和社会输送人才的主要基地.随着高等教育普及与发展,大学办学规模越来越大,招生人数越来越多,教务管理工作越来越复杂,传统的教务管理理念、模式、方法等已经不
研究了苯基三甲氧基硅烷的水解反应,用紫外光谱仪作为检测手段跟踪其水解过程,并分析了水解反应的影响因素。比色皿作为微型反应器,分别考察了不同初始浓度、温度、pH值以及