Styrene-acrylate latex with high glass transition temperature(Tg),low minimum film forming temperature(MFT)and good stability was prepared via core-shell emulsi
【机 构】
：
Department of Material Science and Engineering,Tsinghua University,Beijing 100084,China;Research Ins
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Styrene-acrylate latex with high glass transition temperature(Tg),low minimum film forming temperature(MFT)and good stability was prepared via core-shell emulsion polymerization.With semicontinuous process,high conversion rate of monomer and low gel rate were achieved.The weight ratio of core monomer to shell monomer was approximately 1.35.It is found that many factors such as emulsifiers,initiators,reaction temperature,pH value and polymerization technology have influences on the permormance of styrene-acrylate latex.The prepared latex was characterized by TEM and FTIR.The obtained latex with T of20.57℃,MFT of 5.0℃,and good stability,had good stability of film forming.
其他文献
爱音乐吗?无论是喜欢聆听、欢唱、创作还是演奏,这些超酷的Music装备一定能让你得到最心动的享受
Do you love music? Whether you like listening, singing, writing or pl
A new rheocasting process,Low Superheat Pouring with a Shear Field(LSPSF),was developed to produce semi-solid slurry for the rheo-forming process.The LSPSF proc
智能变电站继电保护装置能够对变电站内的电力设备故障和运行不正常等状况作出迅速地、有选择地反应,从而将故障设备从系统中切除,以达到不影响无故障设备的正常运行,使得故
针对冶金行业对油脂国产化的迫切需求,从冶金设备油脂使用现状入手,分析并提出油脂替代过程中应考虑的主要原则,结合武钢CSP工作辊用脂成功国产化的实际应用,论述冶金设备油
近年来,学术论文主要研究内容重复发表的现象越来越多。这里说的重复发表指的是将同一研究的课题的结果总结成多篇论
In recent years, there are more and more phenomena
随着经济的不断发展,我国城镇化进程脚步加快,随之城市人口激增,导致用电需求不断提升,特别是夏季、冬季等用电高峰时期或时段,跳闸更是经常出现的现象.为了有效解决这一问题
A technology for electroless Ni-P deposition on AZ91D from a low cost plating bath containing sulfate nickel was proposed.The seal pretreatment was employed bef
以现场采集的2011年1-8月间25项水质指标及5种投药指标为基础，应用多元数据统计学理论中的主成分分析和聚类分析方法，对武钢北湖污水处理站的进、出水水质及水处理药剂投加情况