Al-Si metal matrix composites (MMCs) reinforced with 20 vol.% alumina-silicate shot fibers (Al2O3-SiO2(sf)) were fabricated by an infiltration squeeze method. P
Amorphous (Nd,Pr)13Fe80Nb1B6 ribbons were crystallized at 670-730°C for 5-25 min to study the effects of isothermal crystallization on their behavior and m