Pr2Fe14B相关论文
采用部分过快淬加后续晶化退火处理的方法,研究了快淬速度和晶化工艺对低稀土含量Pr10.5(FeCoZr)83.5B6粘结磁体磁性能的影响.通过......
Investigation on mechanism of magnetization reversal for nanocrystalline Pr-Fe-B permanent magnets b
磁化配置被 micromagnetic 为 nanocrystalline Pr-Fe-B 永久磁铁在各种各样的磁场下面计算有限元素方法。根据配置在除去磁性过程......
The interfacial defects of hard magnetic Pr2 Fe14 B phase from amorphous to nanostructures have been investigated by pos......
Amorphous (Nd,Pr)13Fe80Nb1B6 ribbons were crystallized at 670-730°C for 5-25 min to study the effects of isothermal......
对比分析了Pr2Fe14B和Nd2Fe14B永磁材料的矫顽力、剩磁、最大磁能积和居里温度等磁性能参量,说明各向同性快淬Pr2Fe14B永磁合金完......
研究了Pr含量对快淬Prx(FeCoZr)94-xB6(x=12.5,12,10.5,9.0)系列粘结磁体磁性能的影响.采用部分过快淬加晶化退火工艺,获得由非晶......