The corrosion behavior and microstructure of Fe78Si9B13 glassy alloy in NaOH and NaCl solutions under a 0.02-T magnetic field were investigated through electroc
A Bi–2.0Zn–0.2Al(wt%) ternary eutectic alloy was prepared using a vacuum melting furnace and a casting furnace. The samples were directionally solidified upwa