对某钢厂80帘线钢在结晶器和凝固末端复合电磁搅拌(M+F-EMS)条件下生产的连铸大方坯的凝固组织进行了研究,从微观组织、成分偏析等方面进行了分析,探讨了凝固末端电磁搅拌对
【机 构】
：
辽宁科技大学材料与冶金学院,大连理工大学材料科学与工程学院,
论文部分内容阅读
对某钢厂80帘线钢在结晶器和凝固末端复合电磁搅拌(M+F-EMS)条件下生产的连铸大方坯的凝固组织进行了研究,从微观组织、成分偏析等方面进行了分析,探讨了凝固末端电磁搅拌对铸坯凝固组织的影响。结果表明,凝固末端电磁搅拌可以明显的细化80帘线钢铸坯中心部位凝固组织,减少了铸坯中心疏松和缩孔,降低了铸坯中心碳、硫偏析。
The solidification microstructure of continuous casting bloom produced by 80 cords of steel in M + F-EMS mold and solidification end was studied. The microstructure and composition segregation were analyzed The effect of electromagnetic stirring at the end of solidification on the solidified structure of billet was discussed. The results show that the electromagnetic stirring at the end of the solidification can obviously refine the solidified structure in the central part of the 80-cord steel billet, reduce the looseness and shrinkage of the center of the billet and reduce the segregation of carbon and sulfur in the center of the billet.
其他文献
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
群众路线的本质是为民、务实、清廉,为民就是为广大客户服务,务实就是要为群众做实事,清廉就是要体现央企责任和形象。为了深入开展党的群众路线教育实践活动,真心实意地为广
分析了铁尾矿配比对矿渣成分设计参数的影响规律,采用高温熔体物性综合测定仪测定熔渣黏度、流动性等高温物化性能。采用主成分分析法和多元线性回归原理,建立了主成分与熔渣
2008年7月27日，柬埔寨第四届全国大选如期举行，11个政党在全国24个省市对123个国会席位展开激烈争夺，812万登记选民中的601万人参加了投票。9月2日，柬埔寨国家选举委员会公布正式大选结果，柬埔寨人民党再次赢得大选，以90个国会席位的压倒多数优势获得单独组阁权。反对党森朗西党实力稳中有升，获得26个国会席位，取代奉辛比克党跃居国会第二大党。与人民党联合执政了15年的老牌政党奉辛比克党近乎
在处置人质事件中,最常用和最理想的方法是谈判,然而谈判不是万能的,实战中有很多因素影响谈判的进程,有的案件根本就谈不下来,遇到这种情况,就要一边谈判一边进行武力处置。
为了揭示硼铁精矿的碳热还原机理,以高纯石墨为还原剂,进行硼铁精矿含碳球团等温还原实验,并采用积分法进行动力学分析.还原温度分别设定为1000、1050、1100、1150、1200、12
针对PMC矿的利用问题,对PMC精矿与司家营矿粉以7∶3配矿比例造球的氧化焙烧行为进行了研究。研究结果表明,当预热时间为10 min、焙烧温度为1 275℃、焙烧时间为20 min时,球团
针对高磷铁矿矿物组成特点,对氟磷灰石与高磷铁矿中脉石相的反应进行了研究,阐明了高磷铁矿在直接还原过程中含磷矿物的碳热还原机理。研究发现:在不配加石墨的情况下,氟磷灰
基于相似原理,按照1∶4对某钢厂100 t底吹氩钢包建立水模型,研究不同底吹位置、吹氩流量对混匀时间和卷渣行为的影响。研究表明:单喷嘴底吹氩,喷嘴位于钢包底部中心0.5R(钢包
以白云鄂博巴润矿为原料,在1 323~1 573 K下,通过热重质谱联用技术研究巴润矿的配碳还原过程以及还原动力学,对比不同矿物在还原过程中以碳的气化反应为限制环节所得到的活化