For the purpose of improving the strength of this dissimilar joint,the present study was carried out to investigate the improvement in intermetallic layer by using a third material foil between the faying edges of the friction stir welded and hybrid welded Al6061-T6/AZ31 alloy plates.The difference in microstructural and mechanical characteristics of friction stir welded and hybrid welded Al6061-T6/AZ31 joint was compared.Hybrid buttwelding of aluminum alloy plate to a magnesium alloy plate was successfully achieved with Ni foil as filler material,while defect-free laser-friction stir welding(FSW) hybrid welding was achieved by using a laser power of 2 kW.Transverse tensile strength of the joint reached about 66% of the Mg base metal tensile strength in the case of hybrid welding with Ni foil and showed higher value than that of the friction stir welded joint with and without the third material foil.This may be due to the presence of less brittle Ni-based intermetallic phases instead of Al12Mg17.
For the purpose of improving the strength of this dissimilar joint, the present study was carried out to to investigate the improvement in intermetallic layer by using a third material foil between the faying edges of the friction stir welded and hybrid welded Al6061-T6 / AZ31 alloy plates The difference in microstructural and mechanical characteristics of friction stir welded and hybrid welded Al6061-T6 / AZ31 joint was compared. Hybrid buttwelding of aluminum alloy plate to a magnesium alloy plate was successfully achieved with Ni foil as filler material, while defect-free laser -friction stir welding (FSW) hybrid welding was achieved by using a laser power of 2 kW. Transverse tensile strength of the joint reached about 66% of the Mg base metal tensile strength in the case of hybrid welding with Ni foil and showed higher value than that of the friction stir welded joint with and without the third material foil. This may be due to the presence of less brittle Ni-based intermetallic phases instead o f Al12Mg17.