摘要:施工现场所用的建筑材料品种繁多,进场需检测,试验的材料检验项目要服从国家、行业及当地建设主管部门(或所属有关部门)的规定。比如混凝土用的水泥,需按批检验其安定性.强度,凝结时间和细度。工程材料试验检测是一项技术性很强的工作,涉及知识内容广泛。本文着重介绍了检测技术流程和水泥安定性检测方法,最后是对建材质量控制措施的介绍。
关键词:建材检测;水泥安定性;试饼法:雷氏法
Abstract: The materials used in the construction site wide variety, approach to detect, material inspection test items must be subordinated to national, industry and local departments in charge of construction (or the relevant departments) regulations. For example, concrete with cement, according to the number of test its stability. The strength, setting time and fineness. Engineering materials testing is a highly technical work, involves the knowledge content widely. This paper introduces the detection process and the cement soundness detection method, finally is to introduce measures to control the quality of building materials.
Key words: building materials testing; cement soundness; pat method: Redwood method
中圖分类号:TU5 文献标识码: 文章编号:
一、建材质量检测技术分析
1.科学取样取样要有代表性,一般是以一批材料不同部位随机抽取规定数量的样品,即不仅取样数量要正确。取样部位及方法也要按规定进行。试样的数量关系到试验结果的准确性,数量过少,取样部位及方法的偏差,都会使试验误差增大,甚至会得出相反的结果;但是,在实际检测中常常出现取样不具有代表性、取样数量不够,取样方法不正确等。
2.一定的外部环境条件温度和湿度对一些建筑材料的性能有很大的影响。故在标准中对材料养护,测试时环境条件有明确规定,只有严格遵守这些规定,试验结果才具有可比性;该试验在一定程度上能反映出环境温度湿度对材料试验的影响,因而要求试验时必须将温、湿度控制在规定范围内。
3.误差度试验方法须严格按标准规定进行。可是有个别试验人员在作钢筋拉伸试验时只试验到试件出现颈缩而不将其拉至断裂,这是不正确的,这样势必造成试验结果的误差,但这不属于试验误差,而是人为造成的误差。钢筋不拉断,其测得的伸长率较规定的试件断后伸长率要低,与标准规定相违背,这是不允许的。试验要求必须准确,以减少误差度。
4.数据处理由于各种原因,同一组试件中有时试验数据结果离散性较大。为使试验结果准确,标准规定对一些材料的试验结果数据有取舍的要求。如水泥胶砂强度抗折试验,当三个强度值中有一个超出平均值土106 的需剔除该数值,以其余两个强度测定值的平均值作为抗折强度结果。若其中有两个测定值超过平均值的±106 时,则以剩下的一个测定值作为抗折强度结果。若3 个测定值全部超过平均值的±106 时,则须重新检验。混凝土和砂浆的抗压试件强度平均值的计算等都有各自的取舍方法。应予注意,切不可简单地把数据相加计算了事。计算后的数据修约的方法按GB/T8170 进行,其尾数要按四舍五入单双法进位,并按标准规定保留数据的位数。二、水泥安定性检测方法解析
水泥的安定性即体积安定性,是指水泥在凝结硬化过程中体积变化的均匀性。如果水泥硬化后产生不均匀的体积变化,即为体积安定性不良,安定性不良会使水泥制品或混凝土构件产生膨胀性裂缝,降低建筑物质量,甚至引起严重事故。
1.引起水泥安定性不良的原因有很多,主要有以下三种:熟料中所含的游离氧化钙过多、熟料中所含的游离氧化镁过多或掺入的石膏过多。熟料中所含的游离氧化钙或氧化镁都是过烧的,熟化很慢,在水泥硬化后才进行熟化,这是一个体积膨胀的化学反应,会引起不均匀的体积变化,使水泥石开裂。当石膏掺量过多时,在水泥硬化后,它还会继续与固态的水化铝酸钙反应生成高硫型水化硫铝酸钙,体积约增大1.5倍,也会引起水泥石开裂。2.国家标准规定:水泥安定性经沸煮法检验(CaO)必须合格;水泥中氧化镁(MgO)含量不得超过5.0%,如果水泥经压蒸安定性试验合格,则水泥中氧化镁的含量允许放宽到6.0%;水泥中三氧化硫(SO3)的含量不得超过3.5%。
3.安定性不合格的水泥应作废品处理,不能用于工程中。检测方法有试饼法和雷氏法,有争议时以雷氏法为准:
用试饼法进行检验时,将制备好的标准稠度的水泥净浆取出约150g,放在涂油的玻璃板上,使其摊开,成饼状,要求试饼制作必须规范,直径过大、过小,边缘钝厚都会影响试验结果。一般试饼,直径以70~80mm、中心厚约10mm,边缘渐薄、表面光滑为规范试饼。煮后安定性试饼用直尺检查不弯曲,用肉眼观察无裂纹的前提下,仅有少量脱皮现象,应判为安定性合格。试饼煮沸前,应检查并记录有无裂缝或弯曲现象。要检查试饼养护温度时间与湿度是否符合要求(湿气养护箱应能使温度控制在20±3℃,湿度大于90%、养护时间为24±2h)。如养护温度太高(大于25℃)或湿度不够,可能在沸煮前就使试饼发生收缩裂纹,特别是在水泥比表面积比较大的情况下更容易发生收缩裂纹(收缩裂纹往往发生在与玻璃接触的试饼底部中间),这时不能认为试样不安定;如养护温度过低(小于15℃),沸煮后可能产生脱皮现象。 当用雷氏法检验时,要用到专门的仪器:雷氏夹。以测量沸煮后的雷氏夹试模的二指针尖端间的距离的增加值来判断安定性是否合格,如果增加值不大于5.0毫米,则称为水泥体积安定性合格。当用试饼法和雷氏夹法测定同一水泥样品出现争议时,以雷氏夹法为准。
三、建筑材料质量控制措施
1、严格检查建筑材料三证为了控制以上材料配件的质量,严把材料进场检验关是一个重要措施。工程所使用的主要材料、成品、半成品、配件、器具和设备必须具有中文质量合格证明文件,规格、型号及性能检测报告应符合国家技术标准或设计要求。进场时应做检查验收,并经监理工程师核查确认。实行生产许可证和安全认证的制度的产品,应有许可证编号和安全认证标志。实行生产许可证和安全认证的制度的产品,在选购前需对产品的生产许可证及安全认证标志原件进行核查,以防复印件伪造,同类产品不同型号不同规格产品要分别核查每个品种的证件,以防冒名顶替以一代十。招标或采购技术要求、产品样品、投标书、合同等重要文件资料要专人妥善保管,甲方工地代表或监理工程师要全面掌握这些资料,货到工地后依据资料核查验收,对产品的型号、规格、性能指标、产地、数量、外观质量进行检查,不符合要求者不许接收。重要的设备、产品,需要特别关注的产品在设备产品加工生产过程中,需要甲方去现场核查监督生产过程。这项工作是甲方工地容易脱节,建设单位材料部门或合同管理部门整个操作过程没有及时通报给监理工程师,资料也没有给监理工程师复印,有时货到现场后没有及时通知监理工程师,材料部门或工地直接将材料接受,都会造成材料进场把关不严。加热管管材生产企业应向设计、安装和建设单位提交下列文件:国家授权机构提供的有效期内的符合相关标准要求的检验报告;产品合格证;有特殊要求的管材,厂家应提供相应说明书。
2、必要的强制性检测为了保证结构安全,治理质量通病,禁堵伪劣材料用于工程,根据设计要求,或规范要求,或主管部门规定,需要进行项目检测。目前一些地区质量检测站常规检测项目有:主体结构(梁、板、柱)砼标号及钢筋数量检测,竣工后房屋空气质量状况检测,钢筋抽样检测,混凝土试块检测,加气块两项性能(外观质量及强度)检测(非必检测项目),瓷砖性能检测,铝合金门窗三性检测等,这些项目都是强制性要求必须检测的项目。四、结束语检测报告是建筑材料检测站的最终产品,检测报告的准确性和可靠性,直接决定了建筑材料是否合格、能否使用,关系到建筑工程的质量和人民生命财产的安全,也关系到建筑材料检测站的企业形象和社会信誉。因此,加强对建材检测技术要求及工作流程的管理,是建筑材料检测站内部质量管理的重要组成部分,是确保建筑材料检测站出具合格检测报告的重要手段,也是建筑工程质量控制的重要环节。
关键词:建材检测;水泥安定性;试饼法:雷氏法
Abstract: The materials used in the construction site wide variety, approach to detect, material inspection test items must be subordinated to national, industry and local departments in charge of construction (or the relevant departments) regulations. For example, concrete with cement, according to the number of test its stability. The strength, setting time and fineness. Engineering materials testing is a highly technical work, involves the knowledge content widely. This paper introduces the detection process and the cement soundness detection method, finally is to introduce measures to control the quality of building materials.
Key words: building materials testing; cement soundness; pat method: Redwood method
中圖分类号:TU5 文献标识码: 文章编号:
一、建材质量检测技术分析
1.科学取样取样要有代表性,一般是以一批材料不同部位随机抽取规定数量的样品,即不仅取样数量要正确。取样部位及方法也要按规定进行。试样的数量关系到试验结果的准确性,数量过少,取样部位及方法的偏差,都会使试验误差增大,甚至会得出相反的结果;但是,在实际检测中常常出现取样不具有代表性、取样数量不够,取样方法不正确等。
2.一定的外部环境条件温度和湿度对一些建筑材料的性能有很大的影响。故在标准中对材料养护,测试时环境条件有明确规定,只有严格遵守这些规定,试验结果才具有可比性;该试验在一定程度上能反映出环境温度湿度对材料试验的影响,因而要求试验时必须将温、湿度控制在规定范围内。
3.误差度试验方法须严格按标准规定进行。可是有个别试验人员在作钢筋拉伸试验时只试验到试件出现颈缩而不将其拉至断裂,这是不正确的,这样势必造成试验结果的误差,但这不属于试验误差,而是人为造成的误差。钢筋不拉断,其测得的伸长率较规定的试件断后伸长率要低,与标准规定相违背,这是不允许的。试验要求必须准确,以减少误差度。
4.数据处理由于各种原因,同一组试件中有时试验数据结果离散性较大。为使试验结果准确,标准规定对一些材料的试验结果数据有取舍的要求。如水泥胶砂强度抗折试验,当三个强度值中有一个超出平均值土106 的需剔除该数值,以其余两个强度测定值的平均值作为抗折强度结果。若其中有两个测定值超过平均值的±106 时,则以剩下的一个测定值作为抗折强度结果。若3 个测定值全部超过平均值的±106 时,则须重新检验。混凝土和砂浆的抗压试件强度平均值的计算等都有各自的取舍方法。应予注意,切不可简单地把数据相加计算了事。计算后的数据修约的方法按GB/T8170 进行,其尾数要按四舍五入单双法进位,并按标准规定保留数据的位数。二、水泥安定性检测方法解析
水泥的安定性即体积安定性,是指水泥在凝结硬化过程中体积变化的均匀性。如果水泥硬化后产生不均匀的体积变化,即为体积安定性不良,安定性不良会使水泥制品或混凝土构件产生膨胀性裂缝,降低建筑物质量,甚至引起严重事故。
1.引起水泥安定性不良的原因有很多,主要有以下三种:熟料中所含的游离氧化钙过多、熟料中所含的游离氧化镁过多或掺入的石膏过多。熟料中所含的游离氧化钙或氧化镁都是过烧的,熟化很慢,在水泥硬化后才进行熟化,这是一个体积膨胀的化学反应,会引起不均匀的体积变化,使水泥石开裂。当石膏掺量过多时,在水泥硬化后,它还会继续与固态的水化铝酸钙反应生成高硫型水化硫铝酸钙,体积约增大1.5倍,也会引起水泥石开裂。2.国家标准规定:水泥安定性经沸煮法检验(CaO)必须合格;水泥中氧化镁(MgO)含量不得超过5.0%,如果水泥经压蒸安定性试验合格,则水泥中氧化镁的含量允许放宽到6.0%;水泥中三氧化硫(SO3)的含量不得超过3.5%。
3.安定性不合格的水泥应作废品处理,不能用于工程中。检测方法有试饼法和雷氏法,有争议时以雷氏法为准:
用试饼法进行检验时,将制备好的标准稠度的水泥净浆取出约150g,放在涂油的玻璃板上,使其摊开,成饼状,要求试饼制作必须规范,直径过大、过小,边缘钝厚都会影响试验结果。一般试饼,直径以70~80mm、中心厚约10mm,边缘渐薄、表面光滑为规范试饼。煮后安定性试饼用直尺检查不弯曲,用肉眼观察无裂纹的前提下,仅有少量脱皮现象,应判为安定性合格。试饼煮沸前,应检查并记录有无裂缝或弯曲现象。要检查试饼养护温度时间与湿度是否符合要求(湿气养护箱应能使温度控制在20±3℃,湿度大于90%、养护时间为24±2h)。如养护温度太高(大于25℃)或湿度不够,可能在沸煮前就使试饼发生收缩裂纹,特别是在水泥比表面积比较大的情况下更容易发生收缩裂纹(收缩裂纹往往发生在与玻璃接触的试饼底部中间),这时不能认为试样不安定;如养护温度过低(小于15℃),沸煮后可能产生脱皮现象。 当用雷氏法检验时,要用到专门的仪器:雷氏夹。以测量沸煮后的雷氏夹试模的二指针尖端间的距离的增加值来判断安定性是否合格,如果增加值不大于5.0毫米,则称为水泥体积安定性合格。当用试饼法和雷氏夹法测定同一水泥样品出现争议时,以雷氏夹法为准。
三、建筑材料质量控制措施
1、严格检查建筑材料三证为了控制以上材料配件的质量,严把材料进场检验关是一个重要措施。工程所使用的主要材料、成品、半成品、配件、器具和设备必须具有中文质量合格证明文件,规格、型号及性能检测报告应符合国家技术标准或设计要求。进场时应做检查验收,并经监理工程师核查确认。实行生产许可证和安全认证的制度的产品,应有许可证编号和安全认证标志。实行生产许可证和安全认证的制度的产品,在选购前需对产品的生产许可证及安全认证标志原件进行核查,以防复印件伪造,同类产品不同型号不同规格产品要分别核查每个品种的证件,以防冒名顶替以一代十。招标或采购技术要求、产品样品、投标书、合同等重要文件资料要专人妥善保管,甲方工地代表或监理工程师要全面掌握这些资料,货到工地后依据资料核查验收,对产品的型号、规格、性能指标、产地、数量、外观质量进行检查,不符合要求者不许接收。重要的设备、产品,需要特别关注的产品在设备产品加工生产过程中,需要甲方去现场核查监督生产过程。这项工作是甲方工地容易脱节,建设单位材料部门或合同管理部门整个操作过程没有及时通报给监理工程师,资料也没有给监理工程师复印,有时货到现场后没有及时通知监理工程师,材料部门或工地直接将材料接受,都会造成材料进场把关不严。加热管管材生产企业应向设计、安装和建设单位提交下列文件:国家授权机构提供的有效期内的符合相关标准要求的检验报告;产品合格证;有特殊要求的管材,厂家应提供相应说明书。
2、必要的强制性检测为了保证结构安全,治理质量通病,禁堵伪劣材料用于工程,根据设计要求,或规范要求,或主管部门规定,需要进行项目检测。目前一些地区质量检测站常规检测项目有:主体结构(梁、板、柱)砼标号及钢筋数量检测,竣工后房屋空气质量状况检测,钢筋抽样检测,混凝土试块检测,加气块两项性能(外观质量及强度)检测(非必检测项目),瓷砖性能检测,铝合金门窗三性检测等,这些项目都是强制性要求必须检测的项目。四、结束语检测报告是建筑材料检测站的最终产品,检测报告的准确性和可靠性,直接决定了建筑材料是否合格、能否使用,关系到建筑工程的质量和人民生命财产的安全,也关系到建筑材料检测站的企业形象和社会信誉。因此,加强对建材检测技术要求及工作流程的管理,是建筑材料检测站内部质量管理的重要组成部分,是确保建筑材料检测站出具合格检测报告的重要手段,也是建筑工程质量控制的重要环节。