【摘 要】
：
The production of MoO_3 from Sarcheshmeh molybdenite concentrate via a pyro-hydrometallurgical process was studied.The molybdenite concentrate and sodium carbon
【机 构】
：
Department of Materials Engineering Islamic Azad University,Department of Materials Engineering Isfa
【出 处】
：
International Journal of Minerals Metallurgy and Materials
论文部分内容阅读
The production of MoO_3 from Sarcheshmeh molybdenite concentrate via a pyro-hydrometallurgical process was studied.The molybdenite concentrate and sodium carbonate were premixed and fused under air atmosphere.Then the fused products were leached in water and the dissolved molybdenum was recovered as ammonium molybdate.The ammonium molybdate was then calcined to produce mo-lybdic oxide.At the fusion stage,the effect of the mass ratio of carbonate to sulfide on the reaction products and the solubility of the products was investigated.The results show that during the fusion,sodium molybdate and sodium sulfate are the final reaction products and sodium sulfide is detected as an intermediate reaction product.By melting at 850℃with 5wt%excess carbonate,the maximum solubility of the products is obtained.The molybdenum is recovered from the solutions as ammonium molybdate.
The production of MoO_3 from Sarcheshmeh molybdenite concentrate was a. The molybdenite concentrate and sodium carbonate were premixed and fused under air atmosphere. The the fused products were leached in water and the dissolved molybdenum was recovered as ammonium molybdate. ammonium molybdate was then calcined to produce mo-lybdic oxide. At the fusion stage, the effect of the mass ratio of carbonate to sulfide on the reaction products and the solubility of the products was investigated. The results show that during the fusion, sodium molybdate and sodium sulfate are the final reaction products and sodium sulfide is detected as an intermediate reaction product. By melting at 850 ° C with 5 wt% excess carbonate, the maximum solubility of the products is obtained. The molybdenum is recovered from the solutions as ammonium molybdate.
其他文献
A series of nanocomposite thin films, composed of Nd2Fe14B and α-Fe, has been prepared by DC-magnetron sputtering combined ion beam sputtering onto Si (100) su
By using the spark plasma sintering process, Ti2AlC/TiAl composite with the addition of Niobium (Nb) was prepared in-situ and the microstructure of Ti2AlC/TiAl
Isothermal and cyclic oxidation behaviors of chromium samples with and without nanometric CeO2 coating were studied at 900 ℃ in air. Scanning electron microsco
CdGd2(WO4)4-δ single crystal was grown using the Czochralskis method. The crystal structure was tetragonal scheelite with lattice parameters a=b=0.5203 nm and
Ceramic microspheres were prepared by using Chinese bauxite as raw materials through the centrifugal spray drying method. The control technology of microsphere
Ni-W-P-CeO2-SiO2 nano-composite coatings were prepared on the carbon steel surface by pulse co-deposition of nickel, tungsten, phosphorus, nano-CeO2 and nano-Si
Investigation into the magnets with different squareness of hysteresis loop (SHL) reveals that the microstructure of sintered NdFeB magnets has great effects on
A novel method was applied to the surface modification of the metal hydride(MH) electrode of MH/Ni batteries. Both sides of the electrode were plated with a thi
Conducting blends of polyacrylonitrile (PAN) copolymer and dodecylbenzene sulfonic acid doped polyaniline (PANI-DBSA) were prepared by solution blending of the
Hollow spheres of hexagonal ferrite BaCo2Fe16O27 were fabricated through a spray pyrolysis technique using co-precipitation ferrite powder precursor as material