The mechanical properties of Al-6Mg alloy with three treatment states (H112, O and cold-extruded states) were investigated at room and high temperatures using an INSTRON machine and a Split Hopkinson Pressure Bar (SHPB). Stress-strain curves of the alloy with different processes were obtained at a quasi-static strain rate of 5×10-4 s-1and dynamic strain rates of 1 400-4 200 s-1, respectively. The results suggest that, at room temperature, the three processed Al-6Mg alloys are all low sensitive to strain rate. The O state Al-6Mg alloy (Al-6Mg-O) exhibits the most ductility, while the cold-extruded Al-6Mg alloy (Al-6Mg-C) displays the highest strength. At elevated temperatures, the yield stresses and the differences in yield stress of the three processed alloys all decrease with increasing temperature under the quasi-static strain rate of 5×10-4 s-1. Based on test results, modified Johnson-Cook (JC) constitutive models for the three processed Al-6Mg alloys were developed. The microstructures before and after deformation were examined by electron backscattered diffraction (EBSD) and further dynamic recrystallization (DRX) at the strain rate of 3 300 s-1 was discussed. The mechanical properties of Al-6Mg alloy with three treatment states (H112, O and cold-extruded states) were investigated at room and high temperatures using an INSTRON machine and a Split Hopkinson Pressure Bar (SHPB). Stress-strain curves of the alloy with different processes were obtained at a quasi-static strain rate of 5 × 10-4 s-1 and dynamic strain rates of 1 400-4 200 s-1, respectively. The results suggest that, at room temperature, the three processed Al- 6Mg alloys are all low sensitive to strain rate. The O state Al-6Mg alloy (Al-6Mg-O) exhibits the most ductility, while the cold-extruded Al-6Mg alloy (Al-6Mg-C) displays the highest strength. At elevated temperatures, the yield stresses and the differences in yield stress of the three processed alloys all decrease with increasing temperature under the quasi-static strain rate of 5 × 10-4 s-1. Based on test results, modified Johnson-Cook ( JC) constitutive models for the three processed Al-6Mg alloys were developed. The microstru ctures before and after deformation were examined by electron backscattered diffraction (EBSD) and further dynamic recrystallization (DRX) at the strain rate of 3 300 s-1 was discussed.