MnxCd1-xln2Te4 (x=0.1) ingot was successfully grown by the modified Bridgman technique, which applied the accelerated crucible rotation technique (ACRT) in Bridgman process, or briefly ACRT-B. The growth interface profile shape and the composition distribution in the MnxCd1-xln2Te4 (x=0.1) ingot were analyzed. Even though the stoichiometric composition was synthesized in the original ingot, the composition has been redistributed during the ACRT-B growth process. Mn and Cd contents decrease while In increases along the longitudinal axis. The partition ratios of solutes Mn, Cd and In at the growth interface are evaluated by a mathematical method based on the experimental data, which are found to be 1.286, 1.926 and 0.729 in α phase growth process, and 1.120, 1.055 and 0.985 in β phase growth process, respectively. In the radial direction, Mn and Cd contents increase while In decreases with the distance from the centerline of the ingot.
MnxCd1-xln2Te4 (x = 0.1) ingot was successfully grown by the modified Bridgman technique, which applied the accelerated crucible rotation technique (ACRT) in Bridgman process, or briefly ACRT-B. The growth interface profile shape and the composition distribution in the MnxCd1 Even though the stoichiometric composition was synthesized in the original ingot, the composition has been redistributed during the ACRT-B growth process. Mn and Cd contents decrease while increasing along the longitudinal axis. Partition ratios of solutes Mn, Cd and In at the growth interface are evaluated by a mathematical method based on the experimental data, which are found to be 1.286, 1.926 and 0.729 in α phase growth process, and 1.120, 1.055 and 0.985 in β phase growth process, respectively. In the radial direction, Mn and Cd contents increase while In with the distance from the centerline of the ingot.