Electrodeposited Ni matrix/Al microparticles or nanoparticles dispersed composite coatings (termed as EMCCs or ENCCs) are developed from a Ni-based electrolyte bath. The Al microparticles are in a size range of 1 -5 μm and the Al nanoparticles in an average size of 75 nm. The Al content in coatings increases with increase in the particle content in the bath. Particle size effect on the degree of codeposition is not significant. However, codeposition of Al nanoparticles instead of microparticles promotes more homogenous growth of Ni deposits on {111}, {200} and {220} planes. The oxidation at 1 050 ℃ of the as-deposited composite coatings shows that at a comparable Al content, ENCC of Ni-Al exhibits a better oxidation resistance than EMCC of Ni-Al due to the fast formation of an alumina scale during the transient stage of oxidation.