【摘 要】
:
CdS thin films were deposited by ILGAR ( ion laygas reaction) method.The effect of annealing temperature under N2 atmosphere on the structural, chemical, topogr
【机 构】
:
Key Laboratory of Advanced Ceramics and Machining Technology
论文部分内容阅读
CdS thin films were deposited by ILGAR ( ion laygas reaction) method.The effect of annealing temperature under N2 atmosphere on the structural, chemical, topographical development and optical and electrical properties of CdS thin films was investigated by XRD, SEM, XPS, UV- VIS and two-probe technique.It is found that the cubic-phase of as-deposited CdS film transforms to hexagonal phase with a perfected orientation along (002) plane at 300 ℃ .The band gap decreases with increasing annealing temperature until 300 ℃ , which is consisteat with the grain growth.The fall of dark and light resistivitiy is obvious with increasing annealing temperature, corresponding to the continuous grain growth and deviation of stoichiometry at higher temperature.The smooth and uniform surface of as- depositedfilms becomes rougher through thermal treatment, which is related to grain growth and sublimation of CdS at a higher annealing temperature.
其他文献
The effect of cobalt on chemical segregation and solution process in three nickel base single crystal superalloys was investigated. Three alloys containing the
The microstructure and superconducting properties of Bi-2223 superconductor fabricated in high magnetic fields were investigated. The results shows that the Bi-
Experiment on seamless tubes of aluminum alloy A6063 with initial thickness deviation of 0-20% was conducted through a free hydraulic bulging with tube ends fre
The stress corrosion sensitivity of 7A52 aluminum alloy was investigated in the artificial sea water through slow stain rate test(SSRT). The stress corrosion cr
Currently requirements of thin-walled tube with small bending radius cause the defects such as wrinkling,overthinning and cross-section distortion more prone to
Aqueous sols and gels of tungstic acid were prepared from Na2WO4 with protonated cation-exchange resin. Nano-tungsten oxide of a microporous lamella was synthes
Because the mechanical performances of 5182 belts used for carbonated drinks cover decrease after baking, the effects of trace addition of V and depression amou
Ba0.6Sr0.4TiO3 (BST) thin films were fabricated on Pt coated Si (100) substrates by sol-gel techniques with molar ratio of (Ba+Sr) to Ti changing from 0.76 to 1
The quantum chemical calculation on four representative combination modes of the favorable growth unit Al6(OH)18(H2O)6of Al(OH)3 crystals and the single unit we
The properties of styrene-butadiene rubber (SBR) reinforced by modified silica was investigated according to national standards. Silica was modified by silane c