LiMnPO4/C composites were synthesized via solid-state reaction with different carbon sources:sucrose,citric acid and oxalic acid.The samples were characterized
【机 构】
：
College of Environmental Science and Engineering, Guilin University of Technology, Guilin 541004, Ch
论文部分内容阅读
LiMnPO4/C composites were synthesized via solid-state reaction with different carbon sources:sucrose,citric acid and oxalic acid.The samples were characterized by X-ray diffraction (XRD),scanning electron microscopy (SEM) and electrochemical performance test.The results of XRD reveal that carbon coating has no effect on the phase of LiMnPO4.The LiMnPO4/C synthesized at 600 ℃ with citric acid as carbon source shows an initial discharge capacity of 117.8 mAh·g-1 at 0.05 C rate.After 30 cycles,the capacity remains 98.2 mAh.g 1.The improved electrochemical properties of LiMnPO4/C is attributed to the decomposition of organic acid during the sintering process.
其他文献
目的:近年来,医患关系日趋紧张,医疗纠纷数量大幅度上升,处理难度加大,赔偿额越来越高,这已成为社会关注的热点。患者对医院的服务越来越不满意,医疗投诉越来越多。目前知情同意原则已应用到医患关系和临床领域,患者的知情同意权的维护逐渐受到公众的关注。所以本论文通过调查统计4家医院2012~2016年4年间的投诉量,筛选出由知情同意问题引发的医疗投诉。再以具体、真实的数据为基础展开阐述,从而分析原因得出结
该文从挂篮荷载计算、施工流程、支座及临时固结施工、挂篮安装及试验、合拢段施工、模板制作安装、钢筋安装、混凝土的浇筑及养生、测量监控等方面人手,介绍了S226海滨大桥
采用表面机械研磨处理技术(Surface mechanical attrition treatment,SMAT)在工业纯Ti的表面制备出一层厚度约30μm纳米结构表层,最表层的平均晶粒尺寸约30nm。随后在常温(25
Sol-gel technology was employed to synthesize nanosized precursors of La-Mg hydrogen storage alloy at different pH values (0.5,1.5,8.0 and 9.0) of reaction solu
孔子与墨子基于社会生活环境、工作属性、人生信念以及技术主张的不同,发展形成了大相径庭的“以道驭技”观、君子塑造观、道器关系认知以及技术功用观,也得到了在我国历史上不同的社会地位评价。本文从社会管理、技术教育传播、生态技术以及艺术美学等技术应用的四个方面出发,综合分析了孔子和墨子在义利关系、君子培养、技术规范、技术信念、生态伦理关怀以及文质关系等理念上的差异,并从历史因素影响方面指出二者技术伦理思想
在应变速率为0.01 ～ 10.00 s-1、变形温度为700～850℃的条件下,通过热压缩实验研究Cu-Ag合金的高温流变行为,发现该合金高温流变应力对温度和应变速率比较敏感,且在不同条件下
以粉煤灰微珠和炭黑为原料,通过微波加热碳热还原法原位合成了SiC/Mullite球体。利用X射线衍射(XRD),场发射扫描电子显微镜(FESEM)对产物进行了物相和结构表征。研究表明:在1
The microstructures and magnetic properties of Ce32.15Co49.36Cu9.84Fe9.65 magnet sintered at the temperatures ranging from 1005 to 1105 ℃ were investigated.The
请下载后查看，本文暂不支持在线获取查看简介。
Please download to view, this article does not support online access to view profile.
根据动态材料模型绘制并分析了不同应变及失稳准则下Ti-50.9％ Ni(原子分数)形状记忆合金的加工图.结果表明,应变量对等轴组织Ti-50.9％ Ni形状记忆合金加工图的影响较大,Ti-50.9