To prepare high wear resistance and high hardness coatings, electro-spark deposition was adopted for depositing an elec trode of a mixture of 92wt%WC+8wt%Co on a cast steel roll substrate. The coating was characterized by classical X-ray diffracto meter (XRD) and scanning electron microscopy (SEM) with energy dispersive X-ray analysis (EDX). The results indicate that the coating shows nanosized particulate structure and dendritic structure including columnar structure and equiaxed structure. The pri mary phases of the coating contain Fe_3W_3C, Co_3W_3C, Fe_2C and Si_2W. The coating has a low friction coefficient of 0.13, its average wear-resistance is 3.3 times that of the cast steel roll substrate and the main mechanism is abrasive wear. The maximum microhard ness value of the coating is about 1573.9 Hv_(0.3) The study reveals that the electro-spark deposition process has the characteristic of better coating quality and the coating has higher wear resistance and hardness.