论文部分内容阅读
在厂党委领导下,我厂工人、干部和技术人员以阶级斗争为纲,坚持党的基本路线,高举鞍钢宪法的光辉旗帜,坚持独立自主、自力更生的方针,组成了以工人为主体的“三结合”攻关小组来解决焊接结构高压气瓶焊缝近缝区微裂纹的问题。在试验过程中得到了冶金部钢铁研究院、大连工学院等单位的大力协助。在攻关过程中,我们共做了17种试验,加工了650多个试样,试验次数达1,200多次,试验计算数据达18,000多个,试验温度从+80℃到-120℃,经过一年多的时间,终于解决了这个问题。这是无产阶级文化大革命的胜利成果。
Under the leadership of the Factory Party Committee, workers, cadres and technical personnel of our factory made use of the class struggle as the key link, adhered to the party’s basic line, held the glorious banner of the Ansteel Constitution, adhered to the principle of independence and self-reliance, "Research Team to Solve the welding structure of high pressure gas cylinder weld crack near the seam area. In the course of the experiment has been the Ministry of Metallurgical Iron and Steel Research Institute, Dalian Institute of Technology and other units of the strong assistance. In the process of tackling the problem, we conducted a total of 17 kinds of tests, processed more than 650 samples, the number of tests reached 1,200 times, the experimental calculation of data reached more than 18,000, the test temperature from +80 ℃ to -120 ℃, after a year More time, finally solved the problem. This is the victory of the Great Proletarian Cultural Revolution.