【摘 要】
：
Main performance of the cement grouting materials made up by Portland cement(PC) and sulphoaluminate cement(SAC) was investigated in this program, a kind of expanding agent(EA) which was mainly constituted by metakaolin and alunite was utilized for the co
【机 构】
：
Key Laboratory of Metallurgical Emission Reduction & Resources Recycling, Ministry of Education, Col
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Main performance of the cement grouting materials made up by Portland cement(PC) and sulphoaluminate cement(SAC) was investigated in this program, a kind of expanding agent(EA) which was mainly constituted by metakaolin and alunite was utilized for the compensation of the shrinkage, the hydration products and micro structure of the grouting materials were researched by X-ray diffraction(XRD) and scanning electron microscopy (SEM). The results showed that a high expansion rate of the grouting materials could be reached as the expanding agent mixed in 6% of PC mass; the addition of SAC in the S2(PC:SAC:EA=34:6:2.25) brought a further improvement of the expansion rate of the grouting materials, the analysis of XRD and SEM showed that due to the reaction of expanding agent and SAC in the grouting materials, more ettringite crystal was generated, which resulted in a higher early strength, the addition of SAC played an expansion and strength reinforcement role in the grouting materials.
其他文献
Power loss of Fe-3%Si grain-oriented silicon steel was measured after ball scribing with different spacing using a self-designed tool. Three different sections of power loss, including hysteresis loss, abnormal loss, and eddy current loss, were measured a
We put forward a protocol combining laser treatment and acid etching to obtain multiscale micro/nano-texture surfaces of titanium alloy implant. Firstly, the operational parameters of the laser were optimized to obtain an optimum current. Secondly, the la
For the purpose of alleviating the adverse effect of paste aging on the properties of corn starch film,a series of electroneutrally quatemized/sulfosuccinylated starches (EQSS) with different degrees of substitution (DS) were synthesized via the quatemiza
Tungsten carbide (WC) nanoparticles were fabricated from a novel refluxing-derived precursor. The precursor was prepared by acid hydrolysis of Na2WO4 with concentrated HCl in water followed by refluxing with ethanol and n-Dedocane, respectively. Then it w
Amorphous La0.7Zn0.3MnO3 (LZMO) films were deposited on p+-Si substrates by sol-gel method at low temperature of 450℃. The Ag/LZMO/p+-Si device exhibits invertible bipolar resistive switching and theRHRS/RLRS was about 104-106 at room temperature which ca