以两轴向经编增强复合材料为研究对象,分别对玻璃纤维增强体以及环氧树脂基体进行了力学性能测试。同时,对两轴向经编复合材料进行了拉伸力学性能测试,并对断裂后的图像进行了分析。最后,对两轴向经编复合材料沿不同轴向的应力应变曲线及试验数据进行了详细分析。最终确定了影响两轴向经编复合材料拉伸性能的主要因素,以及两轴向经编复合材料在拉伸过程中的破坏机制。 Taking the two axial warp-knitted reinforced composites as the research object, the mechanical properties of glass fiber reinforced plastic and epoxy resin matrix were tested respectively. At the same time, the tensile mechanical properties of the two axial warp knitted composites were tested and the images after fracture were analyzed. Finally, the stress-strain curves and experimental data of two axial warp-knitted composites along different axial directions are analyzed in detail. Finally, the main factors influencing the tensile properties of the two-axial warp knitted composites and the failure mechanism of the two-axial warp knitted composites during the stretching process are finally determined.