【摘 要】
：
A new way to prepare SiC whiskers through the induction of carbon fiber was suggested. With the processing steps of opening furnace firstly and then shutting it
【机 构】
：
C/C Composites Technology Research Center
论文部分内容阅读
A new way to prepare SiC whiskers through the induction of carbon fiber was suggested. With the processing steps of opening furnace firstly and then shutting it,rice hall,as the only raw material,was carbonified to get excess quantity of Si in rice hull. After a certain catalyzer was added,SiC whiskers were prepared by means of the induction of carbon fiber. The component and morphology of the whisker were analyzed by XRD,SEM and TEM. The results reveal that the diameters of the whiskers range in 0.5-2 μm and their lengths in 100-500 μm. The whiskers are straight β-SiC crystals with smooth surface. The whisker is homogeneous and its productivity is 100%. Two kinds of formation mechanisms,both VLS mechanism and vapor formation mechanism,are involved during the growth of the whiskers. But the vapor formation mechanism relatively plays a key role.
其他文献
The effects of Zn content on the as-cast microstructure and mechanical properties of Mg-xZn-4A1 alloys containing TiC and rare earth elements were investigated
New liquid free radical-cationic hybrid photopolymer, consisting of acrylate-based photocurable resin and epoxy-based photosensitive resin for stereolithography
The nanostructures of the ball milled FeCo particles were characterized as functions of the ball milling time ( t ) using quantitative X- ray diffraction (XRD),
Continuing the effort to redesign IN718 alloy in order to provide microstructural and mechanical stability beyond 650 ℃, IN718 alloy was modified by increasing
With electron assisted hot filament chemical vapor deposition technology, nanocrystalline diamond films were deposited on polished n-(100)Si wafer surface. The
A new class of electrorheological (ER) material using rare earth (RE=Y) oxide as the substrate, NaNO3-doped Y2O3 materials, were synthesized using Na2CO3 and Y(
MgO single crystal was irradiated by neutron up to a dose of 5.74×1018 cm-2. The radiation damage and its recovery were studied by means of UV-VIS and EM spect
ZnSe/SiO2 composite thin films was prepared by sol-gel method. XRD results indicate the phase structure of ZnSe particles embedded in ZnSe/SiO2 composite thin f
The lead-free piezoelectric ceramics (K0.5Na0.5)NbO3 (abbreviated as KNN) with the relative density of 97.6% were synthesized by press-less sintering owing to t
Superlattices with varying GaN well widths (2, 3, 6, 9 nm) and fixed AlGaN barrier (8 nm) with high Al-content (x=0.65) were grown. Streaky RHEED patterns indic