In this work, La2NiO4+δ–xCe0.55La0.45O2–δ (denoted as LNO–xLDC) with various LDC contents (x = 0, 10, 20, 30, and 40 wt%) were prepared and evaluated as bif
【机 构】
:
School of Materials Science and Engineering,Jingdezhen Ceramic Institute,Jingdezhen 333403,China;Sch
论文部分内容阅读
In this work, La2NiO4+δ–xCe0.55La0.45O2–δ (denoted as LNO–xLDC) with various LDC contents (x = 0, 10, 20, 30, and 40 wt%) were prepared and evaluated as bifunctional oxygen electrodes for reversible solid oxide cells (RSOCs). Compared with the pure LNO, the optimum composition of LNO–30LDC exhibited the lowest polarization resistance (Rp) of 0.53 and 0.12 ?·cm2 in air at 650 and 750 ℃, respectively. The enhanced electrochemical performance of LNO–30LDC oxygen electrode was mainly attributed to the extended triple phase boundary and more oxygen ionic transfer channels. The hydrogen electrode supported single cell with LNO–30LDC oxygen electrode displayed peak power densities of 276, 401, and 521 mW·cm–2 at 700, 750, and 800 ℃, respectively. Moreover, the electrolysis current density of the single cell demonstrated 526.39 mA·cm–2 under 1.5 V at 800 ℃, and the corresponding hydrogen production rate was 220.03 mL·cm–2·h–1. The encouraging results indicated that LNO–30LDC was a promising bifunctional oxygen electrode material for RSOCs.
其他文献
氟橡胶具有优异的耐化学腐蚀和耐高温性能,在航空航天、机械、石油、汽车和军工等领域广泛应用,减小氟橡胶摩擦因数和磨耗量不但能够延长其密封制品使用寿命,还能够提高生产
Three-dimensional (3D) printing technology is becoming a promising method for fabricating highly complex ceramics owing to the arbitrary design and the infinite
A glycine–nitrate self-propagating high-temperature synthesis (SHS) was developed to produce composite MgO–Gd2O3 nanopowders. The X-ray powder diffraction (XR
The resistive switching (RS) mechanism of hybrid organic–inorganic perovskites has not been clearly understood until now. A switchable diode-like RS behavior i
简要回顾建模仿真技术的发展与演变历程,及其在科技进步中所发挥的重要作用。通过数字孪生产生的背景及内涵,揭示其与建模仿真一脉相承的关系。探讨如何借鉴建模仿真理论方法进行数字孪生的构建和评估,从而保证数字孪生的可信。
High performance hydroxyapatite (HA) ceramics with excellent densification and mechanical properties were successfully fabricated by digital light processing (D
In this study, deep-red emitting Mg2TiO4:Mn4+ phosphor ceramics were synthesized by thehigh temperature solid-state reaction method. The ceramics can be excited
Hybrid improper ferroelectric Ca3Ti2O7 and Ca3Ti1.9Ru0.1O7 ceramics were successfully synthesized by conventional solid-state reaction method. Two strongest dif
Porous mullite hollow fiber membranes were prepared with a combined phase-inversion and sintering method, using three sintering additives including yttrium stab
The effect of pyrolytic carbon (PyC) thickness on the tensile property of mini T800 carbon fiber reinforced SiC matrix composites (C/SiC) was studied. PyC inter