The denitrogenation and desulphurization behavior during vacuum induction melting (VIM) refining Ni-base superalloy using CaO crucible was studied. It has been
The influence of quenching water temperature, pre-stretching amount and aging temperature and times on residual stress in 7075 aluminum thick plate was studied