The conversion coating was formed by dipping AA6061 in a fluorotitanate/zirconate acid and amino trimethylene phosphonic acid (ATMP) solution at room temperature. The formation process and the anti-corrosion performance of the conversion coating were investigated using electrochemical test and salt spray test (SST),respectively. The electrochemical test shows that the Zr/Ti and ATMP coating improves the cor-rosion resistance of AA6061 as good as the chromate (Ⅵ) coating.But the results of SST show that the corrosion resistance of Zr/Ti and ATMP coating is not as good as the chromate (Ⅵ) coating.The corrosion area is less than 2% after 72 h.