Direct strain mapping from high resolution transmission electron microscopy images is possible for coherent structures.At proper imaging conditions the intensit
Nanosized amorphous TiO2 powders with a specific surface area of 501 m2.g-1 were prepared by hydrolysis. Aftercalcined at 400℃ for 2 h, the prepared amorphous