摘 要:随着工程建设的迅速发展,各地兴建了大量的混凝土建筑。在混凝土工程施工中,裂缝问题具有普遍性,裂缝一旦形成,就会降低结构的耐久性,使构件的承载力降低,还可能危害建筑物的安全使用。在当前施工中如何克服混凝土裂缝是一件非常重要的事,本文结合施工管理工作经验及存在的问题,对混凝土裂缝的成因进行简单的分析,并对以后的建设施工过程中提出预防措施。
关键词:建筑工程;混凝土裂缝;成因;防治技术
Abstract: With the rapid development of construction, built around a concrete building. In the construction of concrete engineering, crack problems are universal, cracks, once formed, it will reduce the durability of structure, so that the bearing capacity of members to reduce, safe use could damage buildings. How to overcome in the current construction of concrete crack is a very important matter, according to the construction management work experience and the existing problems, analyze the causes of concrete cracks, puts forward the preventive measures and the construction process.
Key words: construction engineering; concrete cracks; causes; prevention and control technology
中图分类号: TV543+.82
1 对混凝土结构裂缝的认识
钢筋混凝土规范规定:有些结构在所处的不同条件下,允许存在一定宽度的裂缝。大量的混凝土工程实践也证明,在混凝土工程中裂缝问题是不可避免的。混凝土通常是带缝工作的,只要采取有效的措施,就能将其危害程度控制在一定的范围之内。我们要尽量减少裂缝的数量和宽度,尤其要避免有害裂缝的出现,从而确保工程质量。
2 混凝土裂缝的分类
混凝土裂缝是混凝土的一种常见病和多发病。病情绝大多数发生于施工阶段,其原因复杂多变,一般可分为微观裂缝和宏观裂缝两大类。[1]
微观裂缝是指肉眼看不到的、混凝土内部固有的一种裂缝,它是不连贯的。宽度一般在0.05mm以下,这种混凝土本身固有的微观裂缝,荷载不超过设计规定的条件下,一般视为无害。
宏观裂缝宽度在0. 05mm以上,并且认为宽度小于0.2-0.3mm的裂缝是无害的,但是这里必须有个前提,即裂缝不再扩展,为最终宽度。
3 混凝土裂缝的成因分析
混凝土是一种轴心抗拉强度很低的脆性材料,混凝土构件在形成过程中,容易受到材料质量、施工工艺、施工环境等诸多因素的影响,当发生环境温度变化、地基不均匀沉降等问题时,混凝土结构很容易产生裂缝,要根本解决混凝土中裂缝问题,还是需要从混凝土裂缝的形成原因入手。
正确判断和分析混凝土裂缝的成因是有效地控制和减少混凝土裂缝产生的最有效的途径。
3.1混凝土的收缩
混凝土具有热胀冷缩的性质,当环境温度发生变化时,就会产生温度变形,由此产生附加应力,当这种应力超过混凝土的抗拉强度时,就会产生裂缝。在工程中,这类裂缝较多见,譬如现浇屋面板上的裂缝,大体积混凝土中,梁、板、柱等小块体构件收缩裂缝。混凝土收缩裂缝危害较大,尤其是暴露在大气中的构筑物,影响更大。由于收缩而产生的微观裂缝一旦发展,则有可能引起结构物的开裂、变形甚至破坏。
3.2混凝土材料及配合比
材料质量引起的裂缝较常见的原因是水泥、砂、石子等质量不合格。若工程上用了这些不合格的材料,轻则蜂窝麻面,重则导致“豆腐渣工程”,所以必须严把材料的质量关。
配合比设计不但直接影响混凝土的抗拉强度,也是造成混凝土开裂不可忽视的原因。配合比不当指水泥用量过大,水灰比大,含砂率不适当,骨料种类不佳,选用外加剂不当等,这几个因素是互相关联的。有关试验资料显示:用水量不变时,水泥用量每增加10%,混凝土收缩增加5%;水泥用量不变时,用水量每增加10%,混凝土强度降低20%;混凝土与钢筋的粘结力降低10%。[2]
商品混凝土浇捣的楼板经常出现裂缝,总结的原因有如下方面:
①、粗细集料含泥量过大,造成混凝土收缩增大。集料颗粒级配
不良或采取不恰当的间断级配,容易造成混凝土收缩的增大,诱导裂缝的产生。
②、骨料粒径越细、针片含量越大,混凝土单方用灰量、用水量增多,收缩量增大。
③、混凝土外加剂、掺和料选择不当、或掺量不当,严重增加混凝土收縮。
④、水泥品种原因,矿渣硅酸盐水泥收缩比普通硅酸盐水泥收缩大。
⑤、水泥等级及混凝土强度等级原因:水泥等级越高、细度越细、早强越高对混凝土开裂影响很大。混凝土设计强度等级越高,混凝土脆性越大、越易开裂。
3.3 沉降裂缝
沉降裂缝主要是由于结构地基土质不均匀、不密实或浸水所致;或者因为模板刚度不够,支撑间距过大或支撑不稳导致。
3.4施工裂缝
由于施工原因造成的裂缝,原因较多,如配制混凝土所采用的材料质量不合格;现场浇捣混凝土时,振捣不当,振捣时间过长或不足;振捣不密实;大体积混凝土浇注,对水化热计算不准,现场降温、保温工作不到位;施工缝留设位置不当,没按规定处理施工缝;现场养护措施不到位,养护时间不够等都会引起施工裂缝。
3.5温度裂缝温度裂缝发生在大体积混凝土结构中。混凝土在硬化过程中,水泥水化产生大量的水化热,聚集在内部的水化热不易散发,这就形成较大的内外温差,使混凝土内部产生压应力,表面产生拉应力,当温差产生的表面拉应力大于混凝土极限抗拉强度时,就会在混凝土表面产生裂缝。
4 混凝土工程裂缝的预防措施
4.1 材料方面
4.1.1 水泥的选择。在施工中一般采用中热或低热水泥,在不影响水泥活性的情况下,要适当减小水泥的细度,并降低混凝土中水泥用量,以降低水化热的放热速度和放热量。决不使用安定性不合格的水泥。
4.1.2 骨料的选择。在选择粗骨料时,可根据施工条件,尽量选用粒径较大、质量优良、级配良好的石子。这样既可以减少用水量,又可以相应减少水泥用量,还可以减少混凝土的收缩和泌水现象。在选择细骨料时,采用平均粒径较大的中粗砂,并要控制砂子的含泥量,从而降低混凝土的干缩,减少水化热量,这对混凝土裂缝的控制有重要作用。
4.1.3 外掺料和外加剂。掺加适量粉煤灰,可减少水泥用量,从而达到降低水化热的目的。掺入适量的减水剂,可有效地增加混凝土的流动性,且能提高水泥水化率,增加混凝土的强度,从而降低水化热,同时可明显延缓水化热释放速度。
4.2 混凝土配合比、配料、搅拌及浇注方面
4.2.1 配合比设计应尽量采用低水灰比,低水泥用量,低用水量。混凝土搅拌过程中,要确保原材料计量准确,搅拌时间应符合规范要求,并严格控制混凝土塌落度,尽量降低混凝土拌合物的出机温度。
4.2.2 浇注分层应合理,振捣应均匀、适度,不得随意留置施工缝。在混凝土浇筑过程中:一是要控制浇注过程质量。浇注过程中振捣时间均匀一致,以表面泛浆为宜,插点要均匀,浇注完毕后,表面要压实抹平。分层浇注,分层振捣,同时要保证上层混凝土在下层初凝前结合紧密。[3]二是要控制浇注时间。尽量避开高温时段浇注。
4.2.3 设计方面。(1)设计中应尽量避免结构断面突变带来的应力集中。如因结构或造型方面原因等而不得已时,应考虑采用加强措施。(2)要解决由于收缩而产生的裂缝,可在混凝土中掺用膨胀剂来补偿混凝土的收缩。(3)建筑平面造型在满足使用要求的前提下力求简单。(4)正确设置变形缝的位置,缝的宽度选择要适当,构造要合理。(5)构件配筋要合理,位置要准确,间距要适当。
4.2.4施工方面。(1)加强地基的检查和验收,保证其承载力。(2)加强混凝土的早期养护,并适当延长养护时间。(3)大体积混凝土施工,应做好温度测控工作,采取有效的保温措施,保证构件内外温差不超过规定。(4)钢筋绑扎位置要正确,保护层厚度准确,钢筋表面应洁净,钢筋代换必须考虑对构件抗裂性能的影响。
5、结语
总而言之,建筑工程施工中的混凝土裂缝问题已经成为当前建筑工程施工管理工作的一项重要内容,面对施工裂缝问题,只有不断的加强思想重视和施工技术创新,才能保证施工质量。
参考文献:
[1]李子强.建筑工程施工混凝土裂缝及控制措施[J].新建设:现代物业上旬刊,2012,(02).
[2]罗兆华.浅论关于建筑工程施工中混凝土裂缝的分析[J] .中小企業管理与科技,2010,(22).
[3]张伟.基于建筑工程施工中混凝土裂缝的形成及防治措施分析[J] .城市建设理论研究(电子版),2011,(34).
关键词:建筑工程;混凝土裂缝;成因;防治技术
Abstract: With the rapid development of construction, built around a concrete building. In the construction of concrete engineering, crack problems are universal, cracks, once formed, it will reduce the durability of structure, so that the bearing capacity of members to reduce, safe use could damage buildings. How to overcome in the current construction of concrete crack is a very important matter, according to the construction management work experience and the existing problems, analyze the causes of concrete cracks, puts forward the preventive measures and the construction process.
Key words: construction engineering; concrete cracks; causes; prevention and control technology
中图分类号: TV543+.82
1 对混凝土结构裂缝的认识
钢筋混凝土规范规定:有些结构在所处的不同条件下,允许存在一定宽度的裂缝。大量的混凝土工程实践也证明,在混凝土工程中裂缝问题是不可避免的。混凝土通常是带缝工作的,只要采取有效的措施,就能将其危害程度控制在一定的范围之内。我们要尽量减少裂缝的数量和宽度,尤其要避免有害裂缝的出现,从而确保工程质量。
2 混凝土裂缝的分类
混凝土裂缝是混凝土的一种常见病和多发病。病情绝大多数发生于施工阶段,其原因复杂多变,一般可分为微观裂缝和宏观裂缝两大类。[1]
微观裂缝是指肉眼看不到的、混凝土内部固有的一种裂缝,它是不连贯的。宽度一般在0.05mm以下,这种混凝土本身固有的微观裂缝,荷载不超过设计规定的条件下,一般视为无害。
宏观裂缝宽度在0. 05mm以上,并且认为宽度小于0.2-0.3mm的裂缝是无害的,但是这里必须有个前提,即裂缝不再扩展,为最终宽度。
3 混凝土裂缝的成因分析
混凝土是一种轴心抗拉强度很低的脆性材料,混凝土构件在形成过程中,容易受到材料质量、施工工艺、施工环境等诸多因素的影响,当发生环境温度变化、地基不均匀沉降等问题时,混凝土结构很容易产生裂缝,要根本解决混凝土中裂缝问题,还是需要从混凝土裂缝的形成原因入手。
正确判断和分析混凝土裂缝的成因是有效地控制和减少混凝土裂缝产生的最有效的途径。
3.1混凝土的收缩
混凝土具有热胀冷缩的性质,当环境温度发生变化时,就会产生温度变形,由此产生附加应力,当这种应力超过混凝土的抗拉强度时,就会产生裂缝。在工程中,这类裂缝较多见,譬如现浇屋面板上的裂缝,大体积混凝土中,梁、板、柱等小块体构件收缩裂缝。混凝土收缩裂缝危害较大,尤其是暴露在大气中的构筑物,影响更大。由于收缩而产生的微观裂缝一旦发展,则有可能引起结构物的开裂、变形甚至破坏。
3.2混凝土材料及配合比
材料质量引起的裂缝较常见的原因是水泥、砂、石子等质量不合格。若工程上用了这些不合格的材料,轻则蜂窝麻面,重则导致“豆腐渣工程”,所以必须严把材料的质量关。
配合比设计不但直接影响混凝土的抗拉强度,也是造成混凝土开裂不可忽视的原因。配合比不当指水泥用量过大,水灰比大,含砂率不适当,骨料种类不佳,选用外加剂不当等,这几个因素是互相关联的。有关试验资料显示:用水量不变时,水泥用量每增加10%,混凝土收缩增加5%;水泥用量不变时,用水量每增加10%,混凝土强度降低20%;混凝土与钢筋的粘结力降低10%。[2]
商品混凝土浇捣的楼板经常出现裂缝,总结的原因有如下方面:
①、粗细集料含泥量过大,造成混凝土收缩增大。集料颗粒级配
不良或采取不恰当的间断级配,容易造成混凝土收缩的增大,诱导裂缝的产生。
②、骨料粒径越细、针片含量越大,混凝土单方用灰量、用水量增多,收缩量增大。
③、混凝土外加剂、掺和料选择不当、或掺量不当,严重增加混凝土收縮。
④、水泥品种原因,矿渣硅酸盐水泥收缩比普通硅酸盐水泥收缩大。
⑤、水泥等级及混凝土强度等级原因:水泥等级越高、细度越细、早强越高对混凝土开裂影响很大。混凝土设计强度等级越高,混凝土脆性越大、越易开裂。
3.3 沉降裂缝
沉降裂缝主要是由于结构地基土质不均匀、不密实或浸水所致;或者因为模板刚度不够,支撑间距过大或支撑不稳导致。
3.4施工裂缝
由于施工原因造成的裂缝,原因较多,如配制混凝土所采用的材料质量不合格;现场浇捣混凝土时,振捣不当,振捣时间过长或不足;振捣不密实;大体积混凝土浇注,对水化热计算不准,现场降温、保温工作不到位;施工缝留设位置不当,没按规定处理施工缝;现场养护措施不到位,养护时间不够等都会引起施工裂缝。
3.5温度裂缝温度裂缝发生在大体积混凝土结构中。混凝土在硬化过程中,水泥水化产生大量的水化热,聚集在内部的水化热不易散发,这就形成较大的内外温差,使混凝土内部产生压应力,表面产生拉应力,当温差产生的表面拉应力大于混凝土极限抗拉强度时,就会在混凝土表面产生裂缝。
4 混凝土工程裂缝的预防措施
4.1 材料方面
4.1.1 水泥的选择。在施工中一般采用中热或低热水泥,在不影响水泥活性的情况下,要适当减小水泥的细度,并降低混凝土中水泥用量,以降低水化热的放热速度和放热量。决不使用安定性不合格的水泥。
4.1.2 骨料的选择。在选择粗骨料时,可根据施工条件,尽量选用粒径较大、质量优良、级配良好的石子。这样既可以减少用水量,又可以相应减少水泥用量,还可以减少混凝土的收缩和泌水现象。在选择细骨料时,采用平均粒径较大的中粗砂,并要控制砂子的含泥量,从而降低混凝土的干缩,减少水化热量,这对混凝土裂缝的控制有重要作用。
4.1.3 外掺料和外加剂。掺加适量粉煤灰,可减少水泥用量,从而达到降低水化热的目的。掺入适量的减水剂,可有效地增加混凝土的流动性,且能提高水泥水化率,增加混凝土的强度,从而降低水化热,同时可明显延缓水化热释放速度。
4.2 混凝土配合比、配料、搅拌及浇注方面
4.2.1 配合比设计应尽量采用低水灰比,低水泥用量,低用水量。混凝土搅拌过程中,要确保原材料计量准确,搅拌时间应符合规范要求,并严格控制混凝土塌落度,尽量降低混凝土拌合物的出机温度。
4.2.2 浇注分层应合理,振捣应均匀、适度,不得随意留置施工缝。在混凝土浇筑过程中:一是要控制浇注过程质量。浇注过程中振捣时间均匀一致,以表面泛浆为宜,插点要均匀,浇注完毕后,表面要压实抹平。分层浇注,分层振捣,同时要保证上层混凝土在下层初凝前结合紧密。[3]二是要控制浇注时间。尽量避开高温时段浇注。
4.2.3 设计方面。(1)设计中应尽量避免结构断面突变带来的应力集中。如因结构或造型方面原因等而不得已时,应考虑采用加强措施。(2)要解决由于收缩而产生的裂缝,可在混凝土中掺用膨胀剂来补偿混凝土的收缩。(3)建筑平面造型在满足使用要求的前提下力求简单。(4)正确设置变形缝的位置,缝的宽度选择要适当,构造要合理。(5)构件配筋要合理,位置要准确,间距要适当。
4.2.4施工方面。(1)加强地基的检查和验收,保证其承载力。(2)加强混凝土的早期养护,并适当延长养护时间。(3)大体积混凝土施工,应做好温度测控工作,采取有效的保温措施,保证构件内外温差不超过规定。(4)钢筋绑扎位置要正确,保护层厚度准确,钢筋表面应洁净,钢筋代换必须考虑对构件抗裂性能的影响。
5、结语
总而言之,建筑工程施工中的混凝土裂缝问题已经成为当前建筑工程施工管理工作的一项重要内容,面对施工裂缝问题,只有不断的加强思想重视和施工技术创新,才能保证施工质量。
参考文献:
[1]李子强.建筑工程施工混凝土裂缝及控制措施[J].新建设:现代物业上旬刊,2012,(02).
[2]罗兆华.浅论关于建筑工程施工中混凝土裂缝的分析[J] .中小企業管理与科技,2010,(22).
[3]张伟.基于建筑工程施工中混凝土裂缝的形成及防治措施分析[J] .城市建设理论研究(电子版),2011,(34).