【摘 要】
：
Si-Al-Y co-deposition coatings were prepared on Ti-Al alloy by pack cementation processes at 1 050 ℃ for 4 h with different halide activators in the packs for enhancing the high temperature oxidation resistance of Ti-Al alloy. The structure, constituent p
【机 构】
：
School of Materials Science & Engineering, North Minzu University, Yinchuan 750021, China;School of
【出 处】
：
武汉理工大学学报（材料科学版）（英文版）
论文部分内容阅读
Si-Al-Y co-deposition coatings were prepared on Ti-Al alloy by pack cementation processes at 1 050 ℃ for 4 h with different halide activators in the packs for enhancing the high temperature oxidation resistance of Ti-Al alloy. The structure, constituent phases, formation process and oxidation behavior of the coatings were investigated. The experimental results showed that the coatings prepared respectively with NaF and NH4Cl as activators were composed of a (Ti, X) 5Si4, (Ti, X) 5Si3 (X represents Nb and Cr), and TiSi2 outer layer, a TiAl2 inner layer and an Al-rich interdiffusion zone. However, the constituent phases changed into TiSi2 in the outer layer and (Ti, X) 5Si4 and (Ti, X) 5Si3 phases were observed in the middle layer of the coating prepared with AlCl3·6H2O activator. Among the halide activators studied, the coating prepared with AlCl3·6H2O was thicker and denser, which is the only suitable activator for pack Si-Al-Y co-deposition coatings on a Ti-Al alloy. The oxidation results show that the coating can protect the Ti-Al alloy from oxidation at 1000 ℃ in air for at least 80 h. The excellent oxidation resistance of the coating is attributed to the formation of a dense scale mainly consisted of TiO2, SiO2 and Al2O3.
其他文献
A novel gap-plasmon of Fe3O4@Ag core-shell nanoparticles for surface enhanced fluorescence detection of Rhodamine B (RB) was developed.Fe3O4@Ag core-shell nanostructures with Ag shell and Fe3O4 core were synthetized by self-assembled method with the assis
Learning from the process of biominerals formation provides tremendous ideas for developing advanced synthesis techniques.According to the structure formation of tooth enamel,a recombinant amelogenin his-AmelⅩ was designed and constructed.The protein was
Wear-resistant cladding plates consisting of a substrate (Q345 R) and a clad layer (BTW1) were bonded through hot rolling at the temperature of 1 200 ℃ and a rolling speed of 0.5 m/s. The microhardness of the cladding plate was also tested after being hea
The lap joints of Fe-based metallic glass ribbons were carried by resistance spot welding, and the microstructures of spot welds were investigated by X-ray diffraction and transmission electron microscopy. The results indicated that the perfect formations
The influences of nano silica (NS) on the hydration and microstructure development of steam cured cement high volume fly ash (40 wt％, CHVFA) system were investigated. The compressive strength of mortars was tested with different NS dosage from 0 to 4％. Re
Molecular structures of polycarboxylate (PCE) superplasticizer significantly affect the rheological properties of cement paste. Consequently, we employed self-synthesized PCE copolymers with different carboxylic densities to investigate their influence on
The foamed polypropylene (PP) with excellent mechanical and thermal insulating properties was reinforced by blending chlorinated polyethylene (CPE), followed by compression molding foaming in cross-link. The effects of CPE on the foaming behavior, thermal
Mg/Al/Fe layered double hydroxide (MAF-LDH1) was prepared by solvothermal method with the sodium dodecyl sulfate as the template,and the ethanol system was benefit to growth of sample.The nature in the resulting MAF-LDH was investigated by X-ray diffracti
This work focuses on the dynamic rheological behavior of low water-to-binder ratio cement mortars blended with fly ash microspheres (FAM) or silica fume (SF). The initial slump flow of each group has been controlled at similar values by adjusting the supe
The deformation behavior and formability of gradient nano-grained (GNG) AISI 304 stainless steel in uniaxial and biaxial states were investigated by means of tensile test and small punch test (SPT). The GNG top layer was fabricated on coarse grains (CG) A