摘要:后浇带的施工范围日益广泛。 从使用的构件位置上看,可适用于房屋建筑工程的地下室底板、 外墙、 内墙、 顶板、 楼层的楼板,房屋及大型构筑物的基础以及大型设备基础;从房屋建筑工程的功能和形体上看,不仅用于高层主楼与低层裙房连接处,对于超长的多层或高层框架结构,虽不存在沉降问题,但为解决钢筋混凝土的收缩变形或混凝土的收缩应力,也采用后浇收缩带或后浇温度带。 因此,后浇带的施工问题也必须引起高度重视。本文对建筑物后浇带的设置与施工技术进行论述,并对后浇带施工中需注意的事项进行相应的总结。
关键词:建筑工程;后浇带;施工技术
Abstract: the construction of the pouring belt wide range. From the use of components on the position, can be applied to the design of the housing construction project, outer wall, interior wall, roof, floor of floor, houses and large structures and the basis of large equipment foundation; From the function of the housing construction project and form, it not only used in high-rise building and lower the skirt building joints and for long multilayer or high-level framework structure, although not exist settlement, but to solve the reinforced concrete contraction deformation or concrete's shrinkage stress, also USES the pouring contraction band or the pouring temperature belt. Therefore, of the pouring belt construction problems must be attached. In this paper, the building of the pouring belt Settings and construction technology is discussed, and the construction of the pouring belt matters that should pay attention to during corresponding conclusion.
Keywords: building engineering; Of the pouring belt; Construction technology
后澆带就是指在现浇整体钢筋混凝土结构中, 只在施工期间保留的临时性沉降收缩变形缝并根据工程条件,保留一定时间后,再用混凝土浇筑密实成为连续整体、 无沉降缝和收缩缝的结构。在建筑工程中,通过设置后浇带来解决设计中考虑沉降差异或钢筋混凝土的收缩变形以及混凝土的温度应力等问题。后浇带的设置,必须考虑结构的合理性和施工上的方便, 否则也会产生附加应力,对结构产生不良影响, 或者引起结合不良而渗漏水。
一、后浇带的设置和施工技术
1、后浇带的设置要求
(1)后浇带的设置, 应考虑有效降低温差和收缩应力的条件下, 通过计算来决定其留置部位和距离。
后浇带宽度为700---1000MM, 间距一般为20---30M, 贯通整个结构的横截面 ,将结构划分为几个独立区段, 但不一定直线通过一个开间, 以避免钢筋100%有搭接接头。 后浇带的设置 ,应考虑有效降低温差和收缩应力的条件下, 通过计算来决定其留置部位和距离。
(2)后浇带共有四种形式 :平直缝、 阶梯缝、 凸形缝和凹形缝。
若设计无明确要求, 采用何种形式应视具体情况而定, 其中地下室外墙一般采用平直缝,并安装钢板止水带。
(3)在施工基础垫层时, 宜将后浇带处基础垫层降低50---100MM。
以便处理施工缝, 清除垃圾和排除积水。雨期施工时, 后浇带应每隔50M 设一集水坑, 以便及时排除雨水和养护用水。
(4)后浇带处的梁板受力钢筋不许断开, 必须贯通。
如果梁、 板跨度不大, 可一次配足钢筋; 如果跨度较大, 可按规定断开, 在补齐混凝土前焊接好。 施工后浇带的位置宜选在结构受力较小的部位, 一般在梁、 板的反弯点附近 ,此位置弯矩不大, 剪力也不大; 也可选在梁、 板的中部, 弯矩虽大, 但剪力很小。
(5)后浇带的断面形式应考虑浇筑混凝土后连接牢固,一般宜避免留直缝。
对于板, 可留斜缝; 对于梁及基础, 可留企口缝, 而企口缝又有多种形式, 可根据结构断面情况确定。
2、后浇带的施工技术与工艺
(1)混泥土浇注时的技术措施
后挠带混凝土施工前, 应清除钢筋表面锈层, 混凝土表面凿毛 (若采用快易伽网或钢丝队网械陈稽解)。 朗混盼的钠, 细办水冲洗。 混凝土浇注厚度应严格按规范和施工方案进行,以免浇注厚度过大造成钢丝网模板侧压力增大而外凸出,造成尺寸偏差。 为了保证混凝土密实, 垂直施工缝处应采用钢钎捣实 。采用钢丝模板的垂直施工缝, 在混凝土浇注和振捣过程中, 应特别注意分层浇注厚度和振捣器距钢丝网模板的距离。为防止混凝土振捣时水泥浆流失严重, 应限制振捣器与模板的距离 (采用¢50 振捣棒时不小于400MM, 采用¢70 振捣器时,不小于 50MM)。对于已硬化的混凝土表面 ,要使用凿毛机处理。 对较严重的蜂窝或孔洞应进行修补。 在后浇带混凝土浇筑前应用喷枪( 用水和空气) 清理表面。
钢筋若采用断离法, 则按设计及规范要求搭接接长或焊接, 有加强附加钢筋的 ,还需视附加钢筋具体位置穿插施工。后浇带两姻混凝土达到设计规定的龄期后, 按照册规定的施工腑和规定的时间, 挠筑后挠带混凝土。 混胜挠筑蹦度应尽量低于主体混凝土挠筑时触。 宜采用微膨胀混凝土, 强度等级宜提高一统。 后浇带施工缝处理自下而上逐层进行, 后挠带混盼强度达到设计要求后, 视工程特点按规定逐层拆除模板。
(2)后浇带垂直施工缝的处理措施
对木模处的垂直施工缝处, 可用高压水冲毛 ;也可根据现场情况和规范要求尽早拆模并及时用人工凿毛。 对采用钢丝网模板的垂直施工缝, 当混凝土达到初凝时( 用手压混凝土表面能出现指纹), 用压力水冲洗、 清除浮浆 ,并使冲洗部位露出骨料, 同时将钢丝网片冲洗干净。 混凝土终凝后将钢丝网拆除 ,立即用高压水再次冲洗施工缝表面 。为此, 在混凝土浇注后应派专人掌握初凝和终凝时间, 以便选择最佳时间进行冲洗。
(3)预防水浸入底板后浇带的措施
为防止底板周围施工积水流进后浇带内, 在后浇带内, 在后浇带两侧50CM宽处, 用砂浆做出宽50MM, 高50---100MM的挡水带。 为防止地下水从垫层上渗, 在后浇带位置垫层上铺二毡三油, 并在浇注底板后浇带混凝土时, 再在底板面浇注一层10CM 厚的素混凝土附加层, 两者同时浇注。
(4)地下室底板、 侧壁后浇带的施工
地下室因为对防水有一定的要求, 所以后浇带的施工是一个非常关键的环节。后浇带应在其两面三刀侧混凝土龄期达到42 后再施工。 后浇带应采用补偿收缩混凝土, 其强度等级不得低于两侧混凝土。 后浇带混凝土养成护时间不得少28d。在地下室后浇带的施工中必须严格按照规范规定的要求进行处理。
(5)地下室顶板后浇带混凝土的浇筑
不同类型后浇带混凝土的浇筑时间不同: 伸缩后浇带视先浇部分混凝土的收缩完成情况而定, 一般为施工后42---60天 ;沉降后浇带宜在建筑物基本完成沉降后进行。 在一些工程中, 设计单位对后浇带的保留时间有非凡要求, 应按设计要求进行保留。 浇筑后浇带混凝土前, 宜在施工缝处铺一层与混凝土内砂浆成分相同的水泥砂浆。 浇筑后浇带混凝土前 ,用水冲洗施工缝, 保持湿润24小时, 并排除混凝土表面积水。 后浇带混凝土必须采用无收缩混凝土, 可采用膨胀水泥配制, 也可采用添加具有膨胀作用的外加剂和普通水泥配制, 混凝土的强度应提高一个等级, 其配合比通过试验确定, 宜掺入早强减水剂,且应认真配制, 精心振捣。 由于膨胀剂的掺量直接影响混凝土的质量, 因此, 要求膨胀剂的称量由专人负责。 所用膨胀剂和外加剂的品种, 应根据工程性质和现场施工条件选择 并事先通过试验确定配合比, 并适当延长掺膨胀剂的混凝土搅拌时间, 以使混凝土搅拌均匀。
二、后浇带施工中需注意的事项
1、后浇收缩带、 后浇温度带等灌注混凝土的时间问题。 前述后浇带主要是指后浇沉降带或者同时也是收缩带和温度带, 即同时起到三种作用。 如果后浇收缩带单独设置,则灌注混凝土的时间宜在楼板浇筑的 60d 之后, 这样估计可以完成混凝土收缩的 60%以上, 如确有困难时也不宜少于30d;且灌注混凝土的时间宜选择在温度较低时, 不宜在热天浇筑冷天留下来的后浇温度带。
一般高层主楼与低层裙房的基础同时施工,对于上部结构的施工,无论是高层主楼与低层裙房同时施工,还是先施工高层,后施工低层,同样要按施工图要求设置施工后浇带。 高层主楼与低层裙房连接的基础梁、 上部结构的梁和板,要预留出施工后浇带,待主楼与裙房主体完工后(有条件时再推迟一些时间),再用微膨胀混凝土将它浇筑起来,使两侧地梁、 上部梁和板连接成一个整体。 这样做能够使高层与低层的差异沉降减少一部分, 因为高层主楼完成之后,一般情况下, 其沉降量已完成最终沉降量的 60%~80%,剩下的沉降量就小得多,这时再补齐施工后浇带混凝土,二者差异沉降量就较小。
2、后浇带两侧的隔断做法。 在施工后浇带处,混凝土虽为后浇,但钢筋不能断。 如果梁、 板跨度不大,可一次配足钢筋;如果跨度较大,可按规定断开,在补齐混凝土前焊接好。 施工后浇带的断面形式应考虑浇筑混凝土后连接牢固,一般宜避免留直缝。 对于板,可留斜缝;对于梁及基础,可留企口缝,而企口缝又有多种形式,可根据结构断面情况确定。 后浇带两侧宜采用钢筋支架铅丝网或单层钢板网隔断, 钢筋支架的钢筋直径及间距设置视构件断面大小而定, 以支撑稳定为原则,铅丝网的网眼一般不宜过大,以避免灌注混凝土时跑浆。 如网眼偏大,可在网外粘贴一层塑料薄膜,并支挡固定好,以承受灌注混凝土时的挤压力,并保证不跑浆,待混凝土凝固后,薄膜即可撕去,钢筋支架亦可除去,而铅丝网则留在后浇带两侧,即永久留在后浇带内。
3、其他有效施工措施。 后浇带处的钢筋应保证位置准确, 对于板的钢筋网下设置垫块,双层钢筋应设置支架;对于梁、 底部钢筋亦应加垫块,上部钢筋一般直径较大,可不用支架,但应在后浇带部位設马道通过, 过往的人员不应直接踩钢筋。 采用钢筋支架铅丝网隔断时,后浇带两侧混凝土应局部干硬一些, 即水灰比小一些,这样既能保证振捣密实,又不会造成跑浆,使侧面混凝土强度和其他混凝土一致 。另外,在浇筑混凝土前应将后浇带处侧面混凝土浮浆凿除,清刷干净,底部碎屑清除彻底。
参考文献:
[1] 陈平. 后浇带施工技术在建筑工程中的应用[J]. 中外建筑, 2008,(04) .
[2] 黄宗文. 后浇带施工技术在建筑工程中的应用[J]. 中国新技术新产品, 2009,(16) .
[3] 赵兴才. 建筑工程中后浇带施工技术的分析及应用[J]. 中国新技术新产品, 2009,(13) .
[4] 钱时华. 对建筑后浇带法施工技术若干问题的研究[J]. 今日科苑, 2009,(16) .
关键词:建筑工程;后浇带;施工技术
Abstract: the construction of the pouring belt wide range. From the use of components on the position, can be applied to the design of the housing construction project, outer wall, interior wall, roof, floor of floor, houses and large structures and the basis of large equipment foundation; From the function of the housing construction project and form, it not only used in high-rise building and lower the skirt building joints and for long multilayer or high-level framework structure, although not exist settlement, but to solve the reinforced concrete contraction deformation or concrete's shrinkage stress, also USES the pouring contraction band or the pouring temperature belt. Therefore, of the pouring belt construction problems must be attached. In this paper, the building of the pouring belt Settings and construction technology is discussed, and the construction of the pouring belt matters that should pay attention to during corresponding conclusion.
Keywords: building engineering; Of the pouring belt; Construction technology
后澆带就是指在现浇整体钢筋混凝土结构中, 只在施工期间保留的临时性沉降收缩变形缝并根据工程条件,保留一定时间后,再用混凝土浇筑密实成为连续整体、 无沉降缝和收缩缝的结构。在建筑工程中,通过设置后浇带来解决设计中考虑沉降差异或钢筋混凝土的收缩变形以及混凝土的温度应力等问题。后浇带的设置,必须考虑结构的合理性和施工上的方便, 否则也会产生附加应力,对结构产生不良影响, 或者引起结合不良而渗漏水。
一、后浇带的设置和施工技术
1、后浇带的设置要求
(1)后浇带的设置, 应考虑有效降低温差和收缩应力的条件下, 通过计算来决定其留置部位和距离。
后浇带宽度为700---1000MM, 间距一般为20---30M, 贯通整个结构的横截面 ,将结构划分为几个独立区段, 但不一定直线通过一个开间, 以避免钢筋100%有搭接接头。 后浇带的设置 ,应考虑有效降低温差和收缩应力的条件下, 通过计算来决定其留置部位和距离。
(2)后浇带共有四种形式 :平直缝、 阶梯缝、 凸形缝和凹形缝。
若设计无明确要求, 采用何种形式应视具体情况而定, 其中地下室外墙一般采用平直缝,并安装钢板止水带。
(3)在施工基础垫层时, 宜将后浇带处基础垫层降低50---100MM。
以便处理施工缝, 清除垃圾和排除积水。雨期施工时, 后浇带应每隔50M 设一集水坑, 以便及时排除雨水和养护用水。
(4)后浇带处的梁板受力钢筋不许断开, 必须贯通。
如果梁、 板跨度不大, 可一次配足钢筋; 如果跨度较大, 可按规定断开, 在补齐混凝土前焊接好。 施工后浇带的位置宜选在结构受力较小的部位, 一般在梁、 板的反弯点附近 ,此位置弯矩不大, 剪力也不大; 也可选在梁、 板的中部, 弯矩虽大, 但剪力很小。
(5)后浇带的断面形式应考虑浇筑混凝土后连接牢固,一般宜避免留直缝。
对于板, 可留斜缝; 对于梁及基础, 可留企口缝, 而企口缝又有多种形式, 可根据结构断面情况确定。
2、后浇带的施工技术与工艺
(1)混泥土浇注时的技术措施
后挠带混凝土施工前, 应清除钢筋表面锈层, 混凝土表面凿毛 (若采用快易伽网或钢丝队网械陈稽解)。 朗混盼的钠, 细办水冲洗。 混凝土浇注厚度应严格按规范和施工方案进行,以免浇注厚度过大造成钢丝网模板侧压力增大而外凸出,造成尺寸偏差。 为了保证混凝土密实, 垂直施工缝处应采用钢钎捣实 。采用钢丝模板的垂直施工缝, 在混凝土浇注和振捣过程中, 应特别注意分层浇注厚度和振捣器距钢丝网模板的距离。为防止混凝土振捣时水泥浆流失严重, 应限制振捣器与模板的距离 (采用¢50 振捣棒时不小于400MM, 采用¢70 振捣器时,不小于 50MM)。对于已硬化的混凝土表面 ,要使用凿毛机处理。 对较严重的蜂窝或孔洞应进行修补。 在后浇带混凝土浇筑前应用喷枪( 用水和空气) 清理表面。
钢筋若采用断离法, 则按设计及规范要求搭接接长或焊接, 有加强附加钢筋的 ,还需视附加钢筋具体位置穿插施工。后浇带两姻混凝土达到设计规定的龄期后, 按照册规定的施工腑和规定的时间, 挠筑后挠带混凝土。 混胜挠筑蹦度应尽量低于主体混凝土挠筑时触。 宜采用微膨胀混凝土, 强度等级宜提高一统。 后浇带施工缝处理自下而上逐层进行, 后挠带混盼强度达到设计要求后, 视工程特点按规定逐层拆除模板。
(2)后浇带垂直施工缝的处理措施
对木模处的垂直施工缝处, 可用高压水冲毛 ;也可根据现场情况和规范要求尽早拆模并及时用人工凿毛。 对采用钢丝网模板的垂直施工缝, 当混凝土达到初凝时( 用手压混凝土表面能出现指纹), 用压力水冲洗、 清除浮浆 ,并使冲洗部位露出骨料, 同时将钢丝网片冲洗干净。 混凝土终凝后将钢丝网拆除 ,立即用高压水再次冲洗施工缝表面 。为此, 在混凝土浇注后应派专人掌握初凝和终凝时间, 以便选择最佳时间进行冲洗。
(3)预防水浸入底板后浇带的措施
为防止底板周围施工积水流进后浇带内, 在后浇带内, 在后浇带两侧50CM宽处, 用砂浆做出宽50MM, 高50---100MM的挡水带。 为防止地下水从垫层上渗, 在后浇带位置垫层上铺二毡三油, 并在浇注底板后浇带混凝土时, 再在底板面浇注一层10CM 厚的素混凝土附加层, 两者同时浇注。
(4)地下室底板、 侧壁后浇带的施工
地下室因为对防水有一定的要求, 所以后浇带的施工是一个非常关键的环节。后浇带应在其两面三刀侧混凝土龄期达到42 后再施工。 后浇带应采用补偿收缩混凝土, 其强度等级不得低于两侧混凝土。 后浇带混凝土养成护时间不得少28d。在地下室后浇带的施工中必须严格按照规范规定的要求进行处理。
(5)地下室顶板后浇带混凝土的浇筑
不同类型后浇带混凝土的浇筑时间不同: 伸缩后浇带视先浇部分混凝土的收缩完成情况而定, 一般为施工后42---60天 ;沉降后浇带宜在建筑物基本完成沉降后进行。 在一些工程中, 设计单位对后浇带的保留时间有非凡要求, 应按设计要求进行保留。 浇筑后浇带混凝土前, 宜在施工缝处铺一层与混凝土内砂浆成分相同的水泥砂浆。 浇筑后浇带混凝土前 ,用水冲洗施工缝, 保持湿润24小时, 并排除混凝土表面积水。 后浇带混凝土必须采用无收缩混凝土, 可采用膨胀水泥配制, 也可采用添加具有膨胀作用的外加剂和普通水泥配制, 混凝土的强度应提高一个等级, 其配合比通过试验确定, 宜掺入早强减水剂,且应认真配制, 精心振捣。 由于膨胀剂的掺量直接影响混凝土的质量, 因此, 要求膨胀剂的称量由专人负责。 所用膨胀剂和外加剂的品种, 应根据工程性质和现场施工条件选择 并事先通过试验确定配合比, 并适当延长掺膨胀剂的混凝土搅拌时间, 以使混凝土搅拌均匀。
二、后浇带施工中需注意的事项
1、后浇收缩带、 后浇温度带等灌注混凝土的时间问题。 前述后浇带主要是指后浇沉降带或者同时也是收缩带和温度带, 即同时起到三种作用。 如果后浇收缩带单独设置,则灌注混凝土的时间宜在楼板浇筑的 60d 之后, 这样估计可以完成混凝土收缩的 60%以上, 如确有困难时也不宜少于30d;且灌注混凝土的时间宜选择在温度较低时, 不宜在热天浇筑冷天留下来的后浇温度带。
一般高层主楼与低层裙房的基础同时施工,对于上部结构的施工,无论是高层主楼与低层裙房同时施工,还是先施工高层,后施工低层,同样要按施工图要求设置施工后浇带。 高层主楼与低层裙房连接的基础梁、 上部结构的梁和板,要预留出施工后浇带,待主楼与裙房主体完工后(有条件时再推迟一些时间),再用微膨胀混凝土将它浇筑起来,使两侧地梁、 上部梁和板连接成一个整体。 这样做能够使高层与低层的差异沉降减少一部分, 因为高层主楼完成之后,一般情况下, 其沉降量已完成最终沉降量的 60%~80%,剩下的沉降量就小得多,这时再补齐施工后浇带混凝土,二者差异沉降量就较小。
2、后浇带两侧的隔断做法。 在施工后浇带处,混凝土虽为后浇,但钢筋不能断。 如果梁、 板跨度不大,可一次配足钢筋;如果跨度较大,可按规定断开,在补齐混凝土前焊接好。 施工后浇带的断面形式应考虑浇筑混凝土后连接牢固,一般宜避免留直缝。 对于板,可留斜缝;对于梁及基础,可留企口缝,而企口缝又有多种形式,可根据结构断面情况确定。 后浇带两侧宜采用钢筋支架铅丝网或单层钢板网隔断, 钢筋支架的钢筋直径及间距设置视构件断面大小而定, 以支撑稳定为原则,铅丝网的网眼一般不宜过大,以避免灌注混凝土时跑浆。 如网眼偏大,可在网外粘贴一层塑料薄膜,并支挡固定好,以承受灌注混凝土时的挤压力,并保证不跑浆,待混凝土凝固后,薄膜即可撕去,钢筋支架亦可除去,而铅丝网则留在后浇带两侧,即永久留在后浇带内。
3、其他有效施工措施。 后浇带处的钢筋应保证位置准确, 对于板的钢筋网下设置垫块,双层钢筋应设置支架;对于梁、 底部钢筋亦应加垫块,上部钢筋一般直径较大,可不用支架,但应在后浇带部位設马道通过, 过往的人员不应直接踩钢筋。 采用钢筋支架铅丝网隔断时,后浇带两侧混凝土应局部干硬一些, 即水灰比小一些,这样既能保证振捣密实,又不会造成跑浆,使侧面混凝土强度和其他混凝土一致 。另外,在浇筑混凝土前应将后浇带处侧面混凝土浮浆凿除,清刷干净,底部碎屑清除彻底。
参考文献:
[1] 陈平. 后浇带施工技术在建筑工程中的应用[J]. 中外建筑, 2008,(04) .
[2] 黄宗文. 后浇带施工技术在建筑工程中的应用[J]. 中国新技术新产品, 2009,(16) .
[3] 赵兴才. 建筑工程中后浇带施工技术的分析及应用[J]. 中国新技术新产品, 2009,(13) .
[4] 钱时华. 对建筑后浇带法施工技术若干问题的研究[J]. 今日科苑, 2009,(16) .