【摘 要】
:
通过对样品La0.3Ca0.7Mn1-xVxO3(x=0.05,0.10,0.134,0.20)的磁化强度-温度(magnetization-temperature, M-T)曲线、电阻率-温度(resistivity-temperature, p-T)曲线、电子自
论文部分内容阅读
通过对样品La0.3Ca0.7Mn1-xVxO3(x=0.05,0.10,0.134,0.20)的磁化强度-温度(magnetization-temperature, M-T)曲线、电阻率-温度(resistivity-temperature, p-T)曲线、电子自旋共振谱的测量,研究了Mn位V掺杂La0.3Ca0.7MnO3体系电荷序和自旋序的影响.结果表明:当0.05≤x≤0.134时,体系存在电荷有序(CO)相,体系自旋序随温度降低发生顺磁(paramagnetism, PM)-荷有序(charge ordering, CO)-反铁磁(antiferromagnetism, AFM)变化.当x=0.20时,电荷有序融化,体系出现再入型自旋玻璃行为.
其他文献
Copolymers mPEG-PCL were prepared and grafted onto polyethylenimine (PEI) to synthesize copolymers mPEG-PCL-g-PEI with low cytotoxicity. The mPEG-PCL-g-PEI coul
The eigenvalue problems of the buckling loads and natural frequencies of a braced beam on an elastic foundation are investigated.The exact solutions for the eig
清道光三年(1823年)太湖流域发生了严重的雨涝灾害.利用《管庭芬日记》保存的降水信息复原了海宁地区逐月降水量,进而综合日记、档案和地方志中天气、雨情、水情、灾情等记录
利用廉价的工业TiO2粉末、通过超声-水热法制备Ti2纳米管,通过刮刀法将TiO2纳米管制各成厚膜气敏传感器.以N2为载气,考察了工作温度、氢气体积分数(下同)对TiO2纳米管氢气敏
采用相空间直接观察法和行为复杂性算法,系统地分析了新型TD-ERCS离散混沌系统产生的伪随机序列的复杂性,得出了其复杂性变化规律.在Kolmogorov复杂性基础上,应用经典的Limpe
针对光子晶体在行波管中的应用,对有限开敞介质光子晶体的模式和带结构进行了分析和计算.分析表明,有限开敞介质光子晶体中所能存在的模式包括EH和HE混合模式,如果是二维光子
采用电子辅助化学气相沉积法(EA-CVD),在含氮气氛中制备出金刚石膜,利用SEM、Raman光谱、EPR测试手段研究了氮气对金刚石膜品质的影响及氮掺杂特性.结果表明,在950℃基片温度
系统研究了负μ材料(MNG)作为包层的对称三层平板波导的传输特性.研究发现,这种波导既支持快波的传播,又支持TE0,TE1模式的慢波传输.其模式特性不同于左手介质波导和传统介质
α,β,γ,δ-四-{4-13-(9-(4-(3-(9-(4-(2-(5,5-二酰氧基甲基-1,3-二噁烷基))))苯基-2,4,8,10-四氧杂螺[5.5]十一烷基)))苯基-2,4,8,10-四氧
以对苯二甲醛、丙二腈、季戊四醇和毗咯为原料,合成了含有螺环结构单元的中间体3-[4-(2,2-二氰基)乙烯基]苯基-9-(4-甲酰基)苯基-2,4,8,10-四氧杂螺[5.5]十一烷(3)和α,β,γ
运用钯元素空心阴极灯和高分辨率光栅单色仪测量了钯原子4d96s和4d95d组态的7个偶宇称能级的发射光谱,确定了这些能级向4d95p组态能级跃迁产生的15条谱线的跃迁分支比.本文大