用Ｘ射线衍射仪和透射电镜研究了粒径和Ｙ，Ｃｅ掺杂元素对ＺｒＯ２纳米粉相结构的影响．结果表明，在室温下平均粒径为～１０ｎｍ的ＺｒＯ２粉单斜相不足２０ｖ．％，而加入２ｍｏｌ％Ｙ２Ｏ３或２ｍｏｌ％ＣｅＯ２可使单斜相更少．试验测得纯ＺｒＯ２，ＺｒＯ２－２ｍｏｌ％ＣｅＯ２，ＺｒＯ２－２ｍｏｌ％Ｙ２Ｏ３纳米粉在室温下单斜相和四方
论文部分内容阅读
用Ｘ射线衍射仪和透射电镜研究了粒径和Ｙ，Ｃｅ掺杂元素对ＺｒＯ２纳米粉相结构的影响．结果表明，在室温下平均粒径为～１０ｎｍ的ＺｒＯ２粉单斜相不足２０ｖ．％，而加入２ｍｏｌ％Ｙ２Ｏ３或２ｍｏｌ％ＣｅＯ２可使单斜相更少．试验测得纯ＺｒＯ２，ＺｒＯ２－２ｍｏｌ％ＣｅＯ２，ＺｒＯ２－２ｍｏｌ％Ｙ２Ｏ３纳米粉在室温下单斜相和四方相保持平衡共存的临界粒径分别为１７．５，２１．０和３２．５ｎｍ．
The effect of particle size and Y and Ce doping elements on the phase structure of ZrO2 nano-powders was investigated by X-ray diffraction and transmission electron microscopy. The results show that the monoclinic phase of ZrO2 powder with an average particle size of ~10 nm at room temperature is less than 20v. %, While the addition of 2 mol% Y2O3 or 2 mol% CeO2 makes the monoclinic phase less. The critical particle sizes of pure ZrO2, ZrO2-2mol% CeO2, ZrO2-2mol% Y2O3 nano-powders co-exist in a monoclinic and tetragonal phase at room temperature are 17.5, 21.0 and 32.5nm, respectively.
其他文献
磁处理方法提高高水充填材料胶结体强度的试验研究霍广新利用磁化水拌制高水充填材料．通过均匀设计试验方法分析磁化参数对高水充填材料胶结体强度的影响并对磁化参数进行优化
朝夕相伴我整整20年的双狮牌三星手表,与我正上大学的女儿同龄。1987年10月,妻子背着出生满月的女儿,和我一起在故乡滇南弥勒县城逛商店。我花195元钱,买了一块双狮牌三星手
给出激光化学汽相沉积法制备a-si_3N_4纳米粒子的原理和经验公式,在特定工艺参数下获得平均粒径为6.5nm的优质a-si_3N_4纳米粒子,用紫外光谱研究其能级结构,发现与小粒子有关
近年来,我科对行气管切开机械通气的清醒患者开展了舒适护理服务,本文探讨舒适护理在行气管切开机械通气的清醒患者的临床应用意义。1资料与方法1.1临床资料2013年1月至2014
国外80年代诞生的一种称为“纳米”的新型材料,是前景非常广阔的跨世纪高新技术材料,它将给世界带来新的产业革命。 据中国科学院固体物理研究所所长、纳米科学专家张立德称
本修改单经国家标准化管理委员会于2008年8月27日以国标委工二函[2008]94号文批准,自2008年9月1日起实施。前言中“本部分的第6章为推荐性,其余全部技术内容为强制性。并应
承德县第一中学创办于1953年,至今已有六十年的办学历史。2011年8月,新一届领导班子上任,承德县一中的历史从此翻开了崭新的一页。他们用人格凝聚人心,用务实打动人心,围绕提
用包套拉伸法和挤压法制备Ｐｄ／Ａｇ纤维复合材料，并通过金相和电子显微镜分别观察其微观结构、测试其性能，如电阻率、硬度、强度及接触电阻等。通过对比其工艺性及所得材料的微观结构和
运用脉冲高能量密度等离子体，在室温下制成立方氮化硼薄膜．沉积薄膜的衬底材料分别选用单晶硅、氯化钠和ＧＣｒ１５轴承钢，用扫描电镜、透射电镜、红外吸收谱仪、扫描Ａｕｇｅｒ微探针等对沉积的薄膜
糖尿病酮症酸中毒是糖尿病的一种严重急性并发症,具有起病急、病情重、变化快等特点,其可使糖尿病患者的病情加重,甚至造成多脏器功能损害或衰竭,因此,及时发现和处理极为重