【摘 要】
：
TiO2/SiO2 aerogels with different molar ratio of SiO2/TiO2 were prepared via non-supercritical method using tetrabutyl titanate and silica sols as raw materials
【机 构】
：
Department of Chemistry
论文部分内容阅读
TiO2/SiO2 aerogels with different molar ratio of SiO2/TiO2 were prepared via non-supercritical method using tetrabutyl titanate and silica sols as raw materials. The samples were characterized by TEM, SEM, BET, IR,XRD and so on. The results indicate that the BET surface area of TiO2/SiO2 aerogels calcined at 550℃ which the photocatalytic degradation of pyridine, the catalytic activities of TiO2/SiO2 aerogels are much higher than that of TiO2 powder. The photocatalytic activity of TiO2/SiO2 aerogels calcined at 800℃ is the optimum. The higher the content of SiO2, the higher the photocatalytic activity of TiO2/SiO2 aerogels. The cost for preparation of the aerogels is greatly reduced by using non-supercritical drying method, and the aerogels are hopefully applied in the treatment of industrial waste water such as coking effluent treatment.
其他文献
The reduction mechanism of stainless steelmaking dust and carbon pellets was investigated. The metal oxides present in the dust were reduced by carbon with a ne
SiCf/Ti-6Al-4V composites were fabricated by the powder-coated fiber method. The precursor fiber was prepared under the optimized parameter, and the composites
Mixture of green petroleum coke, B4C and SiC together with short carbon fiber were employed as starting materials, the mixture was press-formed without any bind
Sapphire crystals with different orientations may cone from implantation of Nb+ ions under different conditions and succedent annealing at reducing atmosphere.
Extraction of the Ligusticum Chuanxiong oil with supercritical CO2 (SC-CO2) was investigated at the temperatures ranging from 55℃ to 70℃ and pressure from 25
Network-induced delay and jitter are key factors causing performance degradation and instability of NCSs (networked control systems). The relationships between
The CCT curves of supercooled austenite were investigated by using THERMECMASTOR-Z simulation machine, test samples refined from 50 kg vacuum induction furnace
Si3 N4/TiC nanocomposite ceramics have been fabricated by hot pressing technique with Al2O3 and Y2O3 as additives.The results showed that well dispersed composi
The structure and disorder-order transformation of NdxFe60.5-xPt39.5(x = 0, 0.5, 1.0, 1.5) alloys were investigated in situ by high temperature X-ray diffractio
In order to improve the quality of the bio-active coating on medical grade CoNiCrMo substrate, hydroxyapatite(HA) coatings were produced via low-temperature dip