The dynamic restoration behavior of 99.99% polycrystalline aluminum was investigated.The deformation was carried out by compression test at 533-773 K and initia
Coarse and agglomerated primary Mg2Si phase in in-situ synthesized Mg2Si/Mg composite with 4%Si was treated in remelting process by means of high intensity ultr
High-speed friction and wear behaviors of bulk Ti3 SiC2 sliding drily against low carbon steel were investigated. Tests were carried out using a block-on-disk t
Continuous SiC(OAl) fibers, named KD-A fibers, were prepared by the melt-spinning of ceramic precursor polyaluminocarbosilane, air-curing, and pyrolizing at 1 3