【摘 要】
：
高锰钢(Mn13)铸件为获得单一奥氏体组织,均需进行水韧处理,以提高使用寿命。以前是铸件浇注后在砂型中冷却,经过开箱清理再进窑加热到1050～1100℃,保温一段时间使奥氏体均匀
【机 构】
：
济南钢铁厂机修分厂,济南钢铁厂机修分厂,
论文部分内容阅读
高锰钢(Mn13)铸件为获得单一奥氏体组织,均需进行水韧处理,以提高使用寿命。以前是铸件浇注后在砂型中冷却,经过开箱清理再进窑加热到1050～1100℃,保温一段时间使奥氏体均匀化后在水中急冷,以获得常温下的奥氏体组织。但由于使用烧煤加热窑,升温速度、保温时间等均掌握不准,经常造成过烧或未烧透而发生淬裂报废,并且处理时间长,消耗大量的
High manganese steel (Mn13) castings In order to obtain a single austenitic structure, are required to deal with water toughening to improve the service life. Casting in the past is cast in the sand cooling, after unpacking and then into the kiln heating to 1050 ~ 1100 ℃, holding the austenite for a period of time after the homogenization in water quenching to obtain austenite at room temperature. However, due to the use of coal-fired heating kiln, heating rate, holding time and so are not allowed to grasp, often resulting in over-burning or not quenched and quench cracking scrap occurs, and the processing time is long, consume a large amount of
其他文献
在一些多轴自动车床加工孔时,常留下不同程度的退刀纹,尤其是较复杂零件,采用钻、镗孔工艺时,较为严重。退刀纹影响产品质量,有时引起产品成批报废。而多轴自动车床纵刀架刀
自“畅通省城”活动84条建议和省人大常委会相关审议意见分别于去年5月底和7月底交办以来,江西省和南昌市政府及有关部门高度重视,全面动员部署,形成了调度有序、督办有方的
近年来,地球化学勘查在我部地质一找矿各阶段工作中获得了广泛应用,已不仅是物、化探专业人员研究和使用的找矿手段,大量地质专业人员正在学习、应用和发展
In recent years
双层涂料碳氮共渗,是我厂发扬自力更生精神,试验出的一种快速碳氮共渗的新工艺。用高频加热,仅用6分钟,渗层就达到0.30～0.50毫米;在炉内加热用30分钟,渗层就达到0.50～0.70毫米
一、全国城乡储蓄的现状据国家统计局公布,1990年末全国城乡储蓄余额为7034亿元,比1985年末增长3.3倍;社会商品零售总额为8255亿元,比1985年增长92％。至于沉淀在广大居民手中
1959年12月中苏专家考察内蒙黄河后套灌区时,苏联专家哈德巴也夫根据灌区潜水在冬季冻结期水位剧烈下降的动态特征(如图1),对河套灌区土壤盐碱化问题提出了如下的看法:1、从
发展山区林业,它不仅是绿化大地、涵养水源、保持水土、调节气候和为社会提供木材及林副产品等造福社会的事业,而且是关系山区经济发展,使群众“靠山吃山”解决生产、生活困
煤与瓦斯突出是一个十分复杂的动力现象,引起突出的原因很多,有待今后深入探讨。本文仅从我局历年发生的煤与瓦斯突出现象,结合矿井地质因素进行分析,对瓦斯的成因及其突出机
文章简单介绍了无锡柴油机厂轴盖自动线多品种生产情况。图5幅。
The article briefly introduced Wuxi Diesel Engine Factory covers an automatic line of more varietie
本文较全面地介绍了Д]100型大功率柴油机上球墨铸铁曲轴的铸制经验。叙述了型砂及芯砂的成分选择,造型及浇注工艺的特点,球墨铸铁曲轴原铁水的熔制及炉料成分。介绍了最适宜