Based on the analyses of aluminum melt flow, solidification, heat transfer during the process of twin-roll casting, a coupling mathematical model of aluminum th
The precipitation processes of γ'and θ phases in Ni75 Al6.5 V18.5 alloy were simulated at different temperatures and the precipitation sequence of two pha
The intermetallic compound Zr1-xHfxCo and Zr1-xScxCo(x=0,0.1,0.2,0.3) were prepared and their suitability for hydrogen storage was investigated. The alloys show
Hydrogen desorption behaviors of zirconium hydride at temperature range of 100-900 ℃ in mixture gases of helium and oxygen was studied by gas phase analysis(GP